PA66 Zytel® 158 NC010Z DUPONT USA
167
- Unit Price:US$ 3,664 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜Glass fiber reinforced
- Application Areas:electrical equipment｜Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 135 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 62.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| melting temperature | ISO 11357-3 | 218 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.7E-04 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.8E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| FMVSS flammability | FMVSS302 | B | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| 1.5mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MediumDensity | 0.900 g/cm³ | ||
| SpecificHeatCapacity of Melt | 2800 J/kg/°C | ||
| ThermalConductivityofMelt | 0.19 W/m/K | ||
| shrinkage rate | MD：3.20mm | 1.1 % | |
| TD | ISO 294-4 | 1.4 % | |
| MD | ISO 294-4 | 1.3 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 3.0 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % | |
| viscosity number | ISO 307 | 120 cm³/g |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | -- ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| 1MHz | IEC 60250 | 3.20 | |
| Dissipation Factor | 100Hz | IEC 60250 | 0.014 |
| 1MHz | IEC 60250 | 0.016 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| Nominal tensile fracture strain | ISO 527-2 | 35 % | |
| flexural modulus | ISO 178 | 2050 Mpa | |
| Tensile modulus | ISO 527-2 | 2400 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.