Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 158 NC010Z DUPONT USA
Zytel®
electrical equipment,Fitness equipment
High temperature resistan,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/158 NC010Z |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak |
| thermal performance | Test Condition | Test Method | DUPONT USA/158 NC010Z |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 62.0 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 135 °C | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| MD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| MD：55to160°C | ISO 11359-2 | 1.7E-04 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1.2E-04 cm/cm/°C | |
| TD：55to160°C | ISO 11359-2 | 1.8E-04 cm/cm/°C | |
| Glass Transition Temperature | ISO 11357-2 | 60.0 °C | |
| melting temperature | ISO 11357-3 | 218 °C |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/158 NC010Z |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 35 % | |
| tensile strength | 屈服 | ISO 527-2 | 62.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 4.5 % |
| flexural modulus | ISO 178 | 2050 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/158 NC010Z |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.60 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.014 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.016 |
| Physical properties | Test Condition | Test Method | DUPONT USA/158 NC010Z |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.3 % |
| ThermalConductivityofMelt | 0.19 W/m/K | ||
| viscosity number | ISO 307 | 120 cm³/g | |
| SpecificHeatCapacity of Melt | 2800 J/kg/°C | ||
| shrinkage rate | MD：3.20mm | 1.1 % | |
| TD | ISO 294-4 | 1.4 % | |
| MediumDensity | 0.900 g/cm³ | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 3.0 % |
| shrinkage rate | MD | ISO 294-4 | 1.3 % |
| flammability | Test Condition | Test Method | DUPONT USA/158 NC010Z |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| Limiting Oxygen Index | ISO 4589-2 | 25 % | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| 0.9mm | UL 94 | HB | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |