PPO NORYL™ GFN30F-801S SABIC INNOVATIVE SHANGHAI
251
- Unit Price:US$ 4,791 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:34MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance｜Glass fiber reinforced｜Hydrolysis resistance
- Application Areas:Lawn equipment｜Garden equipment｜Non specific food｜Outdoor applications｜Electrical field｜Electronic field｜Architectural application field｜Liquid handling｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive External Parts｜Lighting applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 147 °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 139 °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Af | 139 °C | |
| Vicat softening temperature | -- | ASTM D15259 | 147 °C |
| -- | ISO 306/B120 | 149 °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 2.1E-5 cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 2.3E-5 cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 110 to 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 265 to 315 °C | ||
| Temperature in the middle of the barrel | 275 to 320 °C | ||
| Temperature at the front of the material cylinder | 290 to 325 °C | ||
| Spray nozzle temperature | 300 to 325 °C | ||
| Processing (melt) temperature | 300 to 325 °C | ||
| Mold temperature | 80 to 110 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Screw speed | 20 to 100 rpm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 280°C/5.0 kg | ASTM D1238 | 3.2 g/10 min |
| Melt Volume Flow Rate (MVR) | 280°C/5.0 kg | ISO 1133 | 2.00 cm3/10min |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.10 - 0.40 % |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.10 % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 8600 Mpa |
| -- | ISO 527-2/1 | 8200 Mpa | |
| tensile strength | Break3 | ASTM D638 | 130 Mpa |
| Break | ISO 527-2/50 | 110 Mpa | |
| elongation | Break3 | ASTM D638 | 3.0 % |
| Break | ISO 527-2/50 | 2.5 % | |
| Bending modulus | 50.0 mm Span4 | ASTM D790 | 7200 Mpa |
| --5 | ISO 178 | 6800 Mpa | |
| bending strength | --5,6 | ISO 178 | 160 Mpa |
| Yield, 50.0 mm Span4 | ASTM D790 | 160 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 20.0 J |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 590 J/m |
| 23°C8 | ISO 180/1U | 30 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.