PPO GFN30F-801S SABIC INNOVATIVE SHANGHAI
NORYL™
Lawn equipment、Garden equipment、Non specific food、Outdoor applications、Electrical field、Electronic field、Architectural application、Liquid handling、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive External Parts、Lighting applications
enhance、Glass fiber reinforced、Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-801S |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C8 | ISO 180/1U | 30 kJ/m² |
| 23°C | ASTM D4812 | 590 J/m | |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 20.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-801S |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 8600 Mpa |
| elongation | 断裂3 | ASTM D638 | 3.0 % |
| 断裂 | ISO 527-2/50 | 2.5 % | |
| Flexural modulus | --5 | ISO 178 | 6800 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 160 Mpa |
| --5,6 | ISO 178 | 160 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 130 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 8200 Mpa |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 7200 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 110 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-801S |
|---|---|---|---|
| melt mass-flow rate | 280°C/5.0 kg | ASTM D1238 | 3.2 g/10 min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.040 % |
| Melt volume flow rate | 280°C/5.0 kg | ISO 1133 | 2.00 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.10 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.10 - 0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-801S |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 2.1E-5 cm/cm/°C |
| vicat | -- | ISO 306/B120 | 149 °C |
| -- | ASTM D15259 | 147 °C | |
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ISO 11359-2 | 2.3E-5 cm/cm/°C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 147 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 139 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 139 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/GFN30F-801S |
|---|---|---|---|
| drying time | 3.0 to 4.0 hr | ||
| screw speed | 20 to 100 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 275 to 320 °C | ||
| Temperature at the rear of the barrel | 265 to 315 °C | ||
| Processing (melt) temperature | 300 to 325 °C | ||
| drying temperature | 110 to 120 °C | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the front of the material cylinder | 290 to 325 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 80 to 110 °C | ||
| Spray nozzle temperature | 300 to 325 °C |