Material Description

Material Properties:High temperature resistance｜Glass fiber reinforced
Application Areas:Household daily necessities｜Electrical applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180	26 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	8.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	28 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179	9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	170 Mpa
Bending modulus		ISO 178	10300 Mpa
Tensile strain	Break	ISO 527-2	1.5 %
tensile strength	Break	ISO 527-2	110 Mpa
Tensile modulus		ISO 527-2	10500 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 5.0 hr
Processing (melt) temperature			280 to 310 °C
Mold temperature			130 to 155 °C

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	130 °C
RTI Imp		UL 746	120 °C
RTI Elec		UL 746	130 °C
Linear coefficient of thermal expansion	Across Flow : -30 to 30°C	TMA	4.2E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -30 to 30°C	TMA	1.9E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	230 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	265 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.45 g/cm³
Shrinkage rate	横向Flow	Internal Method	0.30 - 0.70 %
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.020 %
Shrinkage rate	Flow	Internal Method	0.10 - 0.40 %

Electrical performance	Test Condition	Test Method	Test Result
High arc combustion index	0.75 mm	UL 746	PLC 0
High arc combustion index	High arc combustion index	1.5 mm	UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 3
Hot wire ignition	0.75 mm	UL 746	PLC 3
Hot wire ignition	Hot wire ignition	1.5 mm	UL 746	PLC 2
Compared to the anti leakage trace index		IEC 60112	PLC 1
Arc resistance		ASTM D495	PLC 6
Dissipation factor	1 MHz	IEC 60250	2.0E-3
Dielectric constant	1 MHz	IEC 60250	3.00
Dielectric strength		ASTM D149	35 KV/mm
Volume resistivity		IEC 60093	> 1.0E+16 ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

SPS XAREC™ S931 IDEMITSU JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet