Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SPS S931 IDEMITSU JAPAN
XAREC™
Household daily necessiti、Electrical applications
High temperature resistan、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 9.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 26 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 28 kJ/m² |
| Mechanical properties | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10500 Mpa | |
| bending strength | ISO 178 | 170 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ISO 178 | 10300 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| Dissipation Factor | 1 MHz | IEC 60250 | 2.0E-3 |
| Volume resistivity | IEC 60093 | > 1.0E+16 ohms·cm | |
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.5 mm | UL 746 | PLC 2 |
| dielectric strength | ASTM D149 | 35 KV/mm | |
| arc resistance | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | 1.5 mm | UL 746 | PLC 0 |
| dielectric constant | 1 MHz | IEC 60250 | 3.00 |
| flammability | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.020 % |
| Shrinkage rate | 横向流量 | 内部方法 | 0.30 - 0.70 % |
| 流量 | 内部方法 | 0.10 - 0.40 % | |
| density | ISO 1183 | 1.45 g/cm³ |
| Thermal performance | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 265 °C |
| Linear coefficient of thermal expansion | 流动 : -30 到 30°C | TMA | 1.9E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 230 °C |
| Linear coefficient of thermal expansion | 横向 : -30 到 30°C | TMA | 4.2E-5 cm/cm/°C |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | IDEMITSU JAPAN/S931 |
|---|---|---|---|
| drying time | 3.0 to 5.0 hr | ||
| Processing (melt) temperature | 280 to 310 °C | ||
| drying temperature | 120 °C | ||
| Temperature | 130 to 155 °C |