PC/ABS Bayblend® FR 3013 011823 COVESTRO SHANGHAI

334

Unit Price:US$ 3,000 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Shanghai port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜Impact modification
Application Areas:Household appliances｜Electronic field｜Electrical field
Color:--
Grade:Injection grade

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
ISO			PC+ABS-FR(40)
Melt viscosity	240°C	ISO 11443-A	155	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180	无断裂
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	31	%
UL flame retardant rating	1.5 mm	UL 94	V-0 5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break, 23°C	ISO 527-2/50	30	%
Tensile strain	Tensile strain	Yield, 23°C	ISO 527-2/50	4.0	%
tensile strength	Break, 23°C	ISO 527-2/50	44.0	Mpa
tensile strength	tensile strength	Yield, 23°C	ISO 527-2/50	61.0	Mpa
Tensile modulus	23°C	ISO 527-2/1	2650	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Suggested injection volume			30 to 70	%
Suggested maximum moisture content			< 0.020	%
Drying time - Dry Air Dryer			4.0	hr
Drying Temperature - Dry Air Dryer			80	°C
Temperature at the rear of the barrel			220 to 230	°C
Temperature in the middle of the barrel			225 to 235	°C
Temperature at the front of the material cylinder			230 to 240	°C
Spray nozzle temperature			255 to 265	°C
Processing (melt) temperature			240 to 270	°C
Mold temperature			60 to 90	°C
Back pressure			5.00 to 15.0	Mpa
Exhaust hole depth			0.025 to 0.075	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	7.6E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	7.5E-5	cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	95.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	89.0	°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	78.0	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	86.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3.00 mm4	ISO 2577	0.40 - 0.60	%
Shrinkage rate	Shrinkage rate	2.00 mm3	ISO 294-4	0.40 - 0.60	%
Melt Volume Flow Rate (MVR)	240°C/5.0 kg	ISO 1133	26.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	IEC 60093	2.0E+18	ohms·cm
Surface resistivity		IEC 60093	5.0E+17	ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Guangzhou Donglai	US$ 3000 /MT

Supplier Join

Get App

Top

PC/ABS Bayblend® FR 3013 011823 COVESTRO SHANGHAI

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index