Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS FR 3013 011823 COVESTRO SHANGHAI
Bayblend®
Household appliances、Electronic field、Electrical field
Flame retardant、Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| tensile strength | 屈服, 23°C | ISO 527-2/50 | 61.0 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2/50 | 30 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2650 Mpa |
| tensile strength | 断裂, 23°C | ISO 527-2/50 | 44.0 Mpa |
| Tensile strain | 屈服, 23°C | ISO 527-2/50 | 4.0 % |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| Volume resistivity | 23°C | IEC 60093 | 2.0E+18 ohms·cm |
| Surface Resistivity | IEC 60093 | 5.0E+17 ohms |
| flammability | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 5VB |
| Limiting Oxygen Index | ISO 4589-2 | 31 % |
| Filling analysis | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| ISO 9660 | PC+ABS-FR(40) | ||
| melt viscosity | 240°C | ISO 11443-A | 155 Pa·s |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| Melt volume flow rate | 240°C/5.0 kg | ISO 1133 | 26.0 cm3/10min |
| Shrinkage rate | 3.00 mm4 | ISO 2577 | 0.40 - 0.60 % |
| 2.00 mm3 | ISO 294-4 | 0.40 - 0.60 % |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 95.0 °C |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 86.0 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 78.0 °C | |
| vicat | -- | ISO 306/B50 | 89.0 °C |
| Linear coefficient of thermal expansion | 横向 : 23 到 55°C | ISO 11359-2 | 7.6E-5 cm/cm/°C |
| 流动 : 23 到 55°C | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| injection | Test Condition | Test Method | COVESTRO SHANGHAI/FR 3013 011823 |
|---|---|---|---|
| Suggested maximum moisture content | < 0.020 % | ||
| Drying time - Dry Air Dryer | 4.0 hr | ||
| Temperature in the middle of the barrel | 225 to 235 °C | ||
| Temperature at the rear of the barrel | 220 to 230 °C | ||
| Processing (melt) temperature | 240 to 270 °C | ||
| Exhaust hole depth | 0.025 to 0.075 mm | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the front of the material cylinder | 230 to 240 °C | ||
| Back pressure | 5.00 to 15.0 Mpa | ||
| Drying Temperature - Dry Air Dryer | 80 °C | ||
| Temperature | 60 to 90 °C | ||
| Spray nozzle temperature | 255 to 265 °C |