PPS DURAFIDE® 6150T6 JAPAN POLYPLASTIC
189
- Unit Price:US$ 4,512 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:100MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜High impact resistance
- Application Areas:Fitness equipment｜Household appliances
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.050 % | |
| melt viscosity | ISO 11443 | 240000 mPa·s | |
| Shrinkage rate | 0.2 % | ||
| 0.6 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 90 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | HF2000/HD9100 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.01 % | |
| density | ISO 1183 | 1.71 g/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527-2 | 155 Mpa | |
| Tensile strain | ISO 527-2 | 1.7 % | |
| Flexural modulus | ISO 178 | 11200 Mpa | |
| bending strength | ISO 178 | 205 Mpa | |
| fracture strain | ISO 527-1 | 1.7 % | |
| tensile strength | ISO 527-1 | 155 Mpa | |
| bending strength | ISO 178 | 205 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 8.0 kJ/m² | |
| Flexural modulus | ISO 178 | 11200 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 155 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 11200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 205 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | 1.7 % |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | ISO 11443 | 240 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 5E-03 | |
| IEC 60250 | 126 sec | ||
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| dielectric strength | IEC 60243-1 | 16 KV/mm | |
| relative permittivity | IEC 60250 | 4.50 | |
| IEC 60250 | 4.40 | ||
| Dissipation Factor | IEC 60250 | 4E-03 | |
| Volume resistivity | ASTM D257/IEC 60093 | 7.0 x 10^ 15 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.71 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 265 °C | |
| Linear coefficient of thermal expansion | 内部方法 | 1E-05 cm/cm/°C | |
| 内部方法 | 4E-05 cm/cm/°C | ||
| ISO 11359-2 | 2 ×10-5/℃ | ||
| 4 ×10-5/℃ | |||
| Heat distortion temperature | ISO 75-1 | 265 | |
| Combustibility (rate) | UL 94 | - | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | - mm/mm.℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.