PPS 6150T6 JAPAN POLYPLASTIC
DURAFIDE®
Fitness equipment、Household appliances
Glass fiber reinforced、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| melt viscosity | 310℃,1000/sec | ISO 11443 | 240 Pa·s |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| ColorNumber | HF2000/HD9100 |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 90 |
| Basic performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| Water absorption rate | 23℃,水中24小时 | ISO 62 | 0.01 % |
| density | ISO 1183 | 1.71 g/cm³ |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 205 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ISO 179/1eA | 8.0 kJ/m² | |
| Flexural modulus | ASTM D790/ISO 178 | 11200 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ISO 178 | 205 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.7 % |
| Flexural modulus | ISO 178 | 11200 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 1.7 % | |
| tensile strength | ASTM D638/ISO 527 | 155 kg/cm²(MPa)[Lb/in²] | |
| ISO 527-2 | 155 Mpa | ||
| fracture strain | ISO 527-1 | 1.7 % | |
| tensile strength | ISO 527-1 | 155 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| Dissipation Factor | 1kHz | IEC 60250 | 4E-03 |
| relative permittivity | 1kHz | IEC 60250 | 4.50 |
| Dissipation Factor | 耐电弧性 | IEC 60250 | 126 sec |
| Volume resistivity | IEC 60093 | 2E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 16 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 4.40 |
| Volume resistivity | ASTM D257/IEC 60093 | 7.0 x 10^ 15 Ω.cm | |
| Dissipation Factor | 1MHz | IEC 60250 | 5E-03 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Physical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.71 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.01 % |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| Shrinkage rate | 流动方向，80℃×2mmt | 0.2 % | |
| 垂直方向，80℃×2mmt | 0.6 % | ||
| Water absorption rate | 23°C,24hr | ISO 62 | 0.050 % |
| melt viscosity | 310°C,1000sec^-1 | ISO 11443 | 240000 mPa·s |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/6150T6 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 垂直方向 | 4 ×10-5/℃ | |
| Combustibility (rate) | UL 94 | - | |
| Linear coefficient of thermal expansion | 流动方向 | ISO 11359-2 | 2 ×10-5/℃ |
| TD | 内部方法 | 4E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 265 °C |
| Linear coefficient of thermal expansion | MD | 内部方法 | 1E-05 cm/cm/°C |
| ASTM D696/ISO 11359 | - mm/mm.℃ | ||
| Heat distortion temperature | 1.8MPa，HDT | ISO 75-1 | 265 |