COC

COC TOPAS® 8007F-600 JAPAN POLYPLASTIC

283

Unit Price:US$ 15,675 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Dimensional stability｜Chemical resistance
Application Areas:LCD application｜Optical applications
Color:--
Grade:Food grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
gloss	60°,70.0μm,铸造薄膜	ISO 2813	>100
turbidity	70.0μm,铸造薄膜	ISO 14782	>2.0 %
Refractive index		ISO 489	1.53 °C
Transmittance rate	2000μm	ISO 13468-2	91 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	63 Mpa
Elongation at Break	23°C	ISO 527-2	4.5 %
Tensile modulus	23°C	ISO 527-2	2600 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	2.6 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	20 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Glass transition temperature		ISO 11357-2	78.0 °C
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	75 °C
Vicat softening temperature		ISO 306/B50	80 °C
Vicat softening temperature	Vicat softening temperature	玻璃转化温度	ISO 11357-2	78 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	190°C/2.16kg	ISO 1133	1.8 g/10min
melt mass-flow rate	melt mass-flow rate	230°C/2.16kg	ISO 1133	10 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	2.00 cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	230°C/2.16kg	ISO 1133	11.0 cm3/10min
Water absorption rate	Saturation,23°C	ISO 62	0.010 %
Water absorption rate	Water absorption rate	(23°C,24hr)	ISO 62	0.01 %
melt mass-flow rate	260℃/2.16Kg	ISO 1133	32 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1E+14 Ω.cm
Dielectric constant	23°C	IEC 60250	2.35 1kHz
Dissipation factor	相对漏电起痕指数	IEC 60112	600 V

film	Test Condition	Test Method	Test Result
film thickness			70 µm
Tensile modulus	MD:70μm,铸造薄膜	ISO 527-3/1	2100 Mpa
Tensile modulus	Tensile modulus	TD:70μm,铸造薄膜	ISO 527-3/1	1700 Mpa
tensile strength	MD:Break,70μm,铸造薄膜	ISO 527-3/50	55.0 Mpa
tensile strength	tensile strength	TD:Break,70μm,铸造薄膜	ISO 527-3/50	50.0 Mpa
elongation	MD:Break,70μm,铸造薄膜	ISO 527-3/50	3.4 %
elongation	elongation	TD:Break,70μm,铸造薄膜	ISO 527-3/50	3.4 %
Water vapor permeability	70μm,23°C,CastFilm,85%RH	ASTMF1249	0.10 g·mm/m²/atm/24hr

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.50mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

COC TOPAS® 8007F-600 JAPAN POLYPLASTIC

Material Description

Technical Data Sheet Compare

Technical Data Sheet