Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC 8007F-600 JAPAN POLYPLASTIC
TOPAS®
LCD application、Optical applications
Dimensional stability、Chemical resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| elongation | TD:断裂,70µm,铸造薄膜 | ISO 527-3/50 | 3.4 % |
| Tensile modulus | TD:70µm,铸造薄膜 | ISO 527-3/1 | 1700 Mpa |
| tensile strength | TD:断裂,70µm,铸造薄膜 | ISO 527-3/50 | 50.0 Mpa |
| Water Vapor Transmission Rate | 70µm,23°C,CastFilm,85%RH | ASTMF1249 | 0.10 g·mm/m²/atm/24hr |
| film thickness | 70 µm | ||
| Tensile modulus | MD:70µm,铸造薄膜 | ISO 527-3/1 | 2100 Mpa |
| elongation | MD:断裂,70µm,铸造薄膜 | ISO 527-3/50 | 3.4 % |
| tensile strength | MD:断裂,70µm,铸造薄膜 | ISO 527-3/50 | 55.0 Mpa |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 2.6 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| elongation at break | 23°C | ISO 527-2 | 4.5 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 20 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 63 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| dielectric constant | 23°C | IEC 60250 | 2.35 1kHz |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| optical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| Haze ratio | 70.0µm,铸造薄膜 | ISO 14782 | >2.0 % |
| refractive index | ISO 489 | 1.53 °C | |
| transmittance | 2000μm | ISO 13468-2 | 91 % |
| gloss | 60°,70.0µm,铸造薄膜 | ISO 2813 | >100 |
| Flame retardant performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.00 cm3/10min |
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.01 % |
| melt mass-flow rate | 260℃/2.16Kg | ISO 1133 | 32 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.010 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 1.8 g/10min |
| Melt volume flow rate | 230°C/2.16kg | ISO 1133 | 11.0 cm3/10min |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 10 g/10min |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/8007F-600 |
|---|---|---|---|
| vicat | ISO 306/B50 | 80 °C | |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 75 °C |
| vicat | 玻璃转化温度 | ISO 11357-2 | 78 °C |
| Glass Transition Temperature | ISO 11357-2 | 78.0 °C |