PPO NORYL™ V0150B SABIC INNOVATIVE NANSHA
226
- Unit Price:US$ 4,717 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Chemical resistance｜High rigidity
- Application Areas:Electrical applications｜electrical equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 113 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 140 °C |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 135 °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 130 °C | |
| vicat | ASTM D152511 | 155 °C | |
| -- | ISO 306/A50 | 160 °C | |
| -- | ISO 306/B50 | 145 °C | |
| -- | ISO 306/B120 | 155 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| 140°C12 | IEC 60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| MD：23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| TD：23to80°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.27 W/m/K | |
| RTI Elec | UL 746 | 110 °C | |
| RTI Imp | UL 746 | 105 °C | |
| RTI Str | UL 746 | 115 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| 2.0mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.0mm | IEC 60695-2-13 | 775 °C |
| 2.0mm | IEC 60695-2-13 | 775 °C | |
| 3.0mm | IEC 60695-2-13 | 775 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| 23°C | ISO 179/1eA | 14 kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
| 23°C | ISO 180/1A | 13 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 33 KV/mm |
| 1.60mm,在油中 | IEC 60243-1 | 26 KV/mm | |
| 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm | |
| relative permittivity | 50Hz | IEC 60250 | 2.80 |
| 60Hz | IEC 60250 | 2.80 | |
| 1MHz | IEC 60250 | 2.70 | |
| Dissipation Factor | 50Hz | IEC 60250 | 9E-04 |
| 60Hz | IEC 60250 | 9E-04 | |
| 1MHz | IEC 60250 | 3E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | 1E+15 ohms·cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 3.5 g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 10.0 cm3/10min |
| shrinkage rate | MD：--2 | 内部方法 | 0.50-0.70 % |
| MD：3.20mm | 内部方法 | 0.50-0.70 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.18 % |
| 平衡,23°C,50%RH | ISO 62 | 0.060 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 110 Mpa | |
| Yield,50.0mmSpan | ASTM D790 | 105 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 35.0 mg |
| tensile strength | 屈服 | ASTM D638 | 70.0 Mpa |
| 屈服 | ISO 527-2/50 | 70.0 Mpa | |
| Break | ASTM D638 | 60.0 Mpa | |
| 断裂 | ISO 527-2/50 | 55.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 5.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 4.0 % |
| elongation | 断裂 | ASTM D638 | 7.0 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 10 % |
| flexural modulus | 50.0mmSpan | ASTM D790 | 2550 Mpa |
| ISO 178 | 2400 Mpa | ||
| Tensile modulus | ASTM D638 | 2500 Mpa | |
| ISO 527-2/1 | 2500 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.