PPO V0150B SABIC INNOVATIVE NANSHA
NORYL™
Electrical applications、electrical equipment
High mobility、Chemical resistance、High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 14 kJ/m² |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 50.0 J |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 5.0 kJ/m² |
23°C | ISO 180/1A | 13 kJ/m² |
hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
ball-indentation hardness | H358/30 | ISO 2039-1 | 113 Mpa |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 2500 Mpa | |
elongation | 屈服 | ASTM D638 | 5.0 % |
Flexural modulus | 50.0mmSpan | ASTM D790 | 2550 Mpa |
Tensile strain | 屈服 | ISO 527-2/50 | 4.0 % |
tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
屈服 | ISO 527-2/50 | 70.0 Mpa | |
Tensile modulus | ASTM D638 | 2500 Mpa | |
elongation | 断裂 | ASTM D638 | 7.0 % |
bending strength | Yield,50.0mmSpan | ASTM D790 | 105 Mpa |
tensile strength | Break | ASTM D638 | 60.0 Mpa |
bending strength | ISO 178 | 110 Mpa | |
Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 35.0 mg |
Flexural modulus | ISO 178 | 2400 Mpa | |
tensile strength | 屈服 | ASTM D638 | 70.0 Mpa |
Tensile strain | 断裂 | ISO 527-2/50 | 10 % |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
relative permittivity | 60Hz | IEC 60250 | 2.80 |
dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 33 KV/mm |
relative permittivity | 50Hz | IEC 60250 | 2.80 |
Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 26 KV/mm |
3.20mm,在油中 | IEC 60243-1 | 16 KV/mm | |
relative permittivity | 1MHz | IEC 60250 | 2.70 |
Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
Dissipation Factor | 50Hz | IEC 60250 | 9E-04 |
60Hz | IEC 60250 | 9E-04 | |
1MHz | IEC 60250 | 3E-03 | |
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 775 °C |
UL flame retardant rating | 2.0mm | UL 94 | 5VA |
Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 775 °C |
1.0mm | IEC 60695-2-13 | 775 °C | |
Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
UL flame retardant rating | 1.5mm | UL 94 | V-0 |
Limiting Oxygen Index | ISO 4589-2 | 32 % |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 10.0 cm3/10min |
melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 3.5 g/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.060 % |
Shrinkage rate | MD:--2 | 内部方法 | 0.50-0.70 % |
Water absorption rate | 饱和,23°C | ISO 62 | 0.18 % |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/V0150B |
---|---|---|---|
Heat distortion temperature | 0.45MPa,Unannealed,100mmSpan,HDT | ISO 75-2/Be | 140 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
vicat | ASTM D152511 | 155 °C | |
Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan,HDT | ISO 75-2/Ae | 130 °C |
RTI Str | UL 746 | 115 °C | |
vicat | -- | ISO 306/B120 | 155 °C |
thermal conductivity | ISO 8302 | 0.27 W/m/K | |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
vicat | -- | ISO 306/A50 | 160 °C |
-- | ISO 306/B50 | 145 °C | |
ball-indentation hardness | 140°C12 | IEC 60695-10-2 | Pass |
Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
RTI Imp | UL 746 | 105 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 135 °C |
Linear coefficient of thermal expansion | TD:23to80°C | ISO 11359-2 | 9E-05 cm/cm/°C |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
RTI Elec | UL 746 | 110 °C |