PBT VALOX™ VX5011-7001 SABIC INNOVATIVE SHANGHAI
91
- Unit Price:US$ 3,132 /MT
- Packaging Specification:
- Supply Quantity:25MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low warpage｜Aging resistance｜Filler: Glass fiber reinforced material｜10% filler by weight｜10% filler by weight
- Application Areas:chip｜Electronic and Electrical Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 165 Mpa |
| Rockwell hardness | R计秤 | ISO 2039-2 | 122 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ISO 11359-2 | 7E-05 cm/cm/°C |
| 横向, -40到40℃ | ASTME831 | 9E-05 cm/cm/°C | |
| Flow: 23 to 150 ° C | 23到150℃ | ISO 11359-2 | 3.9E-05 cm/cm/°C |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 4E-05 cm/cm/°C |
| Flow: -40 to 40 ° C | ISO 11359-2 | 3.7E-05 cm/cm/°C | |
| ASTME831 | 4E-05 cm/cm/°C | ||
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 115 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 115 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 135 °C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 175 °C | |
| Horizontal: 23 to 150 ° C | 横向, 23到150℃ | ISO 11359-2 | 1.5E-04 cm/cm/°C |
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 9E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 21 % | |
| Burning wire flammability index | 3.00mm | IEC 60695-2-12 | 850 °C |
| 1.00mm | IEC 60695-2-12 | 750 °C | |
| UL flame retardant rating | 1.60mm | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler | ASTM D229 | 10 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| -30°C | ISO 179/1eA | 4.0 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 37.0 J |
| 23°C | ISO 180/1U | 40 kJ/m² | |
| -30°C | ISO 180/1U | 30 kJ/m² | |
| 23°C | ASTM D4812 | 480 J/m | |
| ISO 180/1A | 6.0 kJ/m² | ||
| -30°C | ASTM D4812 | 470 J/m | |
| 0°C | ISO 180/1A | 5.0 kJ/m² | |
| -30°C | ISO 180/1A | 5.0 kJ/m² | |
| 0°C | ASTM D256 | 47 J/m | |
| 23°C | ASTM D256 | 47 J/m | |
| -30°C | ASTM D256 | 47 J/m | |
| 23°C | ISO 179/1eU | 40 kJ/m² | |
| -30°C | ISO 179/2U | 40 kJ/m² | |
| 23°C | ISO 179/1eA | 4.0 kJ/m² | |
| ISO 179/2C | 6.0 kJ/m² | ||
| -30°C | ISO 179/1eU | 30 kJ/m² | |
| ISO 179/2C | 6.0 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | 260°C,1500sec^-1 | ISO 11443 | 145 Pa·s |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 50Hz | 50Hz | IEC 60250 | 3.00 |
| 100Hz | 100Hz | IEC 60250 | 3.20 |
| 60Hz | 60Hz | IEC 60250 | 3.00 |
| 1MHz | 1MHz | ASTMD150 | 3.10 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| 3.20mm, In oil | IEC 60243-1 | 18 KV/mm | |
| 1.60mm, In oil | IEC 60243-1 | 25 KV/mm | |
| 0.800mm, In oil | IEC 60243-1 | 29 KV/mm | |
| 3.20mm, inoil | ASTM D149 | 18 KV/mm | |
| 16mm, inoyl | ASTM D149 | 25 KV/mm | |
| 0.800mm, inoil | ASTM D149 | 29 KV/mm | |
| volume resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 4 |
| 100Hz | 100Hz | IEC 60250 | 0.016 |
| Compared to the Leakage Tracking Index (CTI) | -- | IEC 60112 | PLC 3 |
| 60Hz | 60Hz | IEC 60250 | 9E-03 |
| 50Hz | 50Hz | IEC 60250 | 9E-03 |
| 1MHz | 1MHz | ASTMD150 | 0.014 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 200°C/3.8kg | ASTM D1238 | 18 g/10min |
| density | ASTMD792 | 1.31 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.15 % | |
| shrinkage rate | TD2 | 内部方法 | 0.50-0.90 % |
| MD:3.20mm | 内部方法 | 0.40-0.60 % | |
| MD1 | 内部方法 | 0.30-0.80 % | |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 75.0 cm3/10min |
| 250°C/5.0kg | ISO 1133 | 50.0 cm3/10min | |
| 250°C/2.16kg | ISO 1133 | 18.0 cm3/10min | |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 85 g/10min |
| 265°C/5.0kg | ASTM D1238 | 85 g/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| yield | ISO 527-2/5 | 3.0 % | |
| ASTM D638 | 3.0 % | ||
| fracture | ISO 527-2/5 | 95.0 Mpa | |
| ASTM D638 | 90.0 Mpa | ||
| yield | ISO 527-2/5 | 95.0 Mpa | |
| ASTM D638 | 90.0 Mpa | ||
| --3 | ASTM D638 | 4600 Mpa | |
| Fracture bending strain | ISO 178 | 5.0 % | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 54.0 mg |
| Yield, 50.0mm span | ASTM D790 | 126 Mpa | |
| --11 | ISO 178 | 130 Mpa | |
| --10 | ISO 178 | 140 Mpa | |
| --9 | ISO 178 | 4000 Mpa | |
| 50.0mm span | ASTM D790 | 3600 Mpa | |
| fracture | ISO 527-2/5 | 3.0 % | |
| ASTM D638 | 3.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.