Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT VX5011-7001 SABIC INNOVATIVE SHANGHAI
VALOX™ 
chip,Electronic and Electrical Applications
Low warpage,Aging resistance,Filler: Glass fiber reinf,10% filler by weight,10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
Ball Pressure TestH358/30ISO 2039-1165 Mpa
Rockwell hardnessR-SaleISO 2039-2122
Supplementary InformationTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
Filling materialASTM D22910 %
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
0.45MPa, unannealed, 3.20mmASTM D648175 °C
0.45MPa, unannealed, 64.0mm spanISO 75-2/Bf135 °C
1.8MPa, unannealed, 3.20mmASTM D648115 °C
1.8MPa, unannealed, 64.0mm span ofISO 75-2/Af115 °C
Ball Pressure Test125°CIEC 60695-10-2Pass
Flow: 23 to 150 ° C23to150℃ISO 11359-23.9E-05 cm/cm/°C
Flow: 23 to 80 ° C23to80℃ISO 11359-24E-05 cm/cm/°C
Flow: -40 to 40 ° CASTME8314E-05 cm/cm/°C
ISO 11359-23.7E-05 cm/cm/°C
Horizontal: 23 to 150 ° CAcross Flow, 23to150℃ISO 11359-21.5E-04 cm/cm/°C
Horizontal: 23 to 80 ° CAcross Flow, 23to80℃ISO 11359-29E-05 cm/cm/°C
Horizontal: -40 to 40 ° CAcross Flow, -40to40℃ISO 11359-27E-05 cm/cm/°C
Across Flow, -40to40℃ASTME8319E-05 cm/cm/°C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
--10ISO 178140 Mpa
--11ISO 178130 Mpa
--3ASTM D6384600 Mpa
50.0mm spanASTM D7903600 Mpa
--9ISO 1784000 Mpa
crackASTM D63890.0 Mpa
ISO 527-2/595.0 Mpa
ASTM D6383.0 %
ISO 527-2/53.0 %
Fracture bending strainISO 1785.0 %
Taber abraser1000Cycles,1000g,CS-17WheelInternal Method54.0 mg
yieldASTM D6383.0 %
ISO 527-2/53.0 %
ASTM D63890.0 Mpa
ISO 527-2/595.0 Mpa
Yield, 50.0mm spanASTM D790126 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
0.800mm,inOilASTM D14929 KV/mm
0.800mm, in oilIEC 60243-129 KV/mm
1.60mm,inOilASTM D14925 KV/mm
1.60mm, in oilIEC 60243-125 KV/mm
100Hz100HzIEC 602500.016
1MHz1MHzASTMD1500.014
3.20mm, inoilASTM D14918 KV/mm
3.20mm, in oilIEC 60243-118 KV/mm
50Hz50HzIEC 602509E-03
60Hz60HzIEC 602509E-03
Compared to the anti leakage trace index--IEC 60112PLC 3
SolutionBIEC 60112PLC 4
High arc combustion indexHAIUL 746PLC 0
Hot wire ignitionHWIUL 746PLC 0
Surface resistivityIEC 60093>1.0E+15 ohms
Volume resistivityASTMD257>1.0E+15 ohms·cm
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
densityASTMD7921.31 g/cm³
melt mass-flow rate266°C/5.0kgASTM D123885 g/10min
265°C/5.0kgASTM D123885 g/10min
200°C/3.8kgASTM D123818 g/10min
Melt Volume Flow Rate (MVR)250°C/2.16kgISO 113318.0 cm3/10min
265°C/5.0kgISO 113375.0 cm3/10min
250°C/5.0kgISO 113350.0 cm3/10min
Shrinkage rateTD2Internal Method0.50-0.90 %
MD:3.20mmInternal Method0.40-0.60 %
MD1Internal Method0.30-0.80 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.10 %
Saturation,23°CISO 620.15 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
0°CASTM D25647 J/m
ISO 180/1A5.0 kJ/m²
23°CASTM D25647 J/m
ISO 179/2C6.0 kJ/m²
ISO 179/1eA4.0 kJ/m²
ISO 179/1eU40 kJ/m²
ASTM D4812480 J/m
ISO 180/1U40 kJ/m²
ISO 180/1A6.0 kJ/m²
-30°CASTM D4812470 J/m
ISO 179/1eU30 kJ/m²
ASTM D25647 J/m
ISO 179/2C6.0 kJ/m²
ISO 180/1A5.0 kJ/m²
ISO 179/1eA4.0 kJ/m²
ISO 179/2U40 kJ/m²
ISO 180/1U30 kJ/m²
Dart impact23°C,TotalEnergyASTM D376337.0 J
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
Melt viscosity260°C,1500sec^-1ISO 11443145 Pa·s
flammabilityTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/VX5011-7001
Burning wire flammability index3.00mmIEC 60695-2-12850 °C
1.00mmIEC 60695-2-12750 °C
Extreme Oxygen IndexISO 4589-221 %
UL flame retardant rating1.60mmUL 94HB