Material Description

Material Properties:Chemical resistance｜Fatigue resistance｜heat-resisting｜Glass fiber reinforced
Application Areas:Electrical field｜Electronic field｜Industrial applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	400°C,1000sec^-1	ASTM D3835	450	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	--	ISO 180	43	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	--	ASTM D4812	640	J/m
Impact strength of cantilever beam gap	--	ISO 180	8.5	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	--	ASTM D256	64	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.8mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ISO 527-2/1A/5	218	Mpa
Tensile modulus	--	ISO 527-2/1A/1	25400	Mpa
Tensile modulus	Tensile modulus	--	ASTM D638	20900	Mpa
shear strength		ASTM D732	103	Mpa
compressive strength		ASTM D695	188	Mpa
bending strength	--	ISO 178	319	Mpa
bending strength	bending strength	--	ASTM D790	321	Mpa
Bending modulus	--	ISO 178	21500	Mpa
Bending modulus	Bending modulus	--	ASTM D790	17900	Mpa
elongation	Break	ISO 527-2/1A/5	1.7	%
elongation	elongation	Break5	ASTM D638	1.7	%
tensile strength	--	ASTM D638	223	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed	ASTM D648	315	°C
Glass transition temperature		ASTM D3418	147	°C
Melting temperature		ASTM D3418	343	°C
Linear coefficient of thermal expansion	MD：-50to50°C	ASTME831	6.7E-06	cm/cm/°C
specific heat	50°C	DSC	1310	J/kg/°C
specific heat	specific heat	200°C	DSC	1810	J/kg/°C
thermal conductivity		ASTMC177	0.37	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24hr	ASTM D570	0.10	%
Shrinkage rate	TD:3.18mm	ASTM D955	1.4-1.6	%
Shrinkage rate	Shrinkage rate	MD:3.18mm	ASTM D955	0.0-0.20	%
melt mass-flow rate	400°C/2.16kg	ASTM D1238	11	g/10min
density		ASTM D792	1.41	g/cm³
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	106

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Jiate	US$ 60560 /MT
Dongguan Sharp Plastic	US$ 63410 /MT
Dongguan Juheng	US$ 79970 /MT
Shenzhen Bowen New Materials	US$ 80220 /MT
Huashang Star (Guangdong)	US$ 80220 /MT

Supplier Join

Get App

Top

PEEK KetaSpire® KT-880 CF30 SOLVAY USA

Material Description

Material Certification

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index