PC/PBT XENOY™  6370-8A6D030 SABIC INNOVATIVE US

284
  • Unit Price:US$ 2,931 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    103MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Chemical resistance｜Low temperature impact resistance
  • Application Areas:Household daily necessities｜Electrical applications｜Automotive Applications
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact23°C,EnergyatPeakLoadASTM D37635.00 J
Dart impact23°C,TotalEnergyASTM D376317.0 J
Impact strength of cantilever beam gap23°CISO 180/1A10 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
bending strengthBreak,50.0mmSpanASTM D790138 Mpa
bending strengthYield,50.0mmSpanASTM D790150 Mpa
Bending modulusISO 1787750 Mpa
bending strengthISO 178154 Mpa
Bending modulus50.0mmSpanASTM D7905380 Mpa
Tensile modulusASTM D6389750 Mpa
Tensile modulusISO 527-2/18500 Mpa
tensile strengthYieldASTM D63897.0 Mpa
tensile strengthYieldISO 527-2/5105 Mpa
tensile strengthBreakASTM D63891.0 Mpa
tensile strengthBreakISO 527-2/53.00 Mpa
Tensile strainYieldASTM D6383.0 %
Tensile strainYieldISO 527-2/53.0 %
Tensile strainBreakASTM D6384.0 %
Tensile strainBreakISO 527-2/5110 %
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af155 °C
Vicat softening temperatureASTM D152512153 °C
Vicat softening temperature--ISO 306/B50148 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648163 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648149 °C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648204 °C
RTI StrUL 746140 °C
Vicat softening temperature--ISO 306/B120150 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8312.7E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：60to138°CASTME8312E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：-40to40°CISO 11359-22.7E-05 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CASTME8311.1E-04 cm/cm/°C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-21.1E-04 cm/cm/°C
RTI ElecUL 746140 °C
RTI ImpUL 746130 °C
Physical propertiesTest ConditionTest MethodTest Result
Specific volumeASTM D7920.700 cm³/g
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Water absorption rate24hrASTM D5700.090 %
Water absorption rateSaturation,23°CISO 620.50 %
Shrinkage rateMD：--3Internal Method0.40-0.50 %
Shrinkage rateTD：--2Internal Method0.40-0.70 %
Shrinkage rateTD：--3Internal Method0.70-0.90 %
melt mass-flow rate250°C/5.0kgASTM D123824 g/10min
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 113312.0 cm3/10min
Melt Volume Flow Rate (MVR)265°C/5.0kgISO 113319.0 cm3/10min
Shrinkage rateMD：--2Internal Method0.30-0.40 %
Electrical performanceTest ConditionTest MethodTest Result
Compared to the anti leakage trace indexCTIUL 746PLC 2
High arc combustion indexHAIUL 746PLC 3
High arc combustion indexHAIUL 746PLC 3
High voltage arc tracing rateHVTRUL 746PLC 1
Arc resistanceASTM D495PLC 5
Dielectric strength3.20mm,inAirASTM D14920 KV/mm
Dielectric constant100HzASTM D1504.00
Dielectric constant1MHzASTM D1504.00
Dissipation factor100HzASTM D1503E-03
Dissipation factor1MHzASTM D1500.020
Dielectric strength1.60mm,in OilASTM D14927 KV/mm
Hot wire ignitionHWIUL 746PLC 1
Volume resistivityASTM D2574.8E+15 ohms·cm
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785109
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.