PC/PBT 6370-8A6D030 SABIC INNOVATIVE US
XENOY™ 
Household daily necessiti、Electrical applications、Automotive Applications
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376317.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
23°CISO 180/1A10 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D37635.00 J
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Rockwell hardnessR级ASTM D785109
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
High Voltage Arc Traceability Rate (HVTR)HVTRUL 746PLC 1
Dissipation Factor100HzASTM D1503E-03
Volume resistivityASTM D2574.8E+15 ohms·cm
Dissipation Factor1MHzASTM D1500.020
High arc combustion index (HAI)HAIUL 746PLC 3
Hot wire ignition (HWI)HWIUL 746PLC 1
dielectric constant1MHzASTM D1504.00
arc resistanceASTM D495PLC 5
dielectric strength3.20mm,inAirASTM D14920 KV/mm
dielectric constant100HzASTM D1504.00
dielectric strength1.60mm,在油中ASTM D14927 KV/mm
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Tensile modulusISO 527-2/18500 Mpa
tensile strength 断裂ISO 527-2/53.00 Mpa
Tensile strain屈服ISO 527-2/53.0 %
bending strengthBreak,50.0mmSpanASTM D790138 Mpa
Tensile strainBreakASTM D6384.0 %
Flexural modulus50.0mm跨距ASTM D7905380 Mpa
tensile strength 屈服ISO 527-2/5105 Mpa
Tensile modulusASTM D6389750 Mpa
bending strength屈服,50.0mm跨距ASTM D790150 Mpa
tensile strength BreakASTM D63891.0 Mpa
bending strengthISO 178154 Mpa
Tensile strainYieldASTM D6383.0 %
Flexural modulusISO 1787750 Mpa
Tensile strain断裂ISO 527-2/5110 %
tensile strength 屈服ASTM D63897.0 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Shrinkage rateTD：--2内部方法0.40-0.70 %
TD：--3内部方法0.70-0.90 %
Water absorption rate24hrASTM D5700.090 %
Melt volume flow rate250°C/5.0kgISO 113312.0 cm3/10min
Water absorption rate平衡,23°C,50%RHISO 620.15 %
饱和,23°CISO 620.50 %
Shrinkage rateMD：--2内部方法0.30-0.40 %
Specific volumeASTM D7920.700 cm³/g
Shrinkage rateMD：--3内部方法0.40-0.50 %
Melt volume flow rate265°C/5.0kgISO 113319.0 cm3/10min
melt mass-flow rate250°C/5.0kgASTM D123824 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
vicatASTM D152512153 °C
Heat distortion temperature1.8MPa,未退火,6.40mm，HDTASTM D648149 °C
Linear coefficient of thermal expansionTD：-40到40°CISO 11359-21.1E-04 cm/cm/°C
MD：60to138°CASTME8312E-05 cm/cm/°C
MD：-40到40°CISO 11359-22.7E-05 cm/cm/°C
Heat distortion temperature0.45MPa,未退火,6.40mm，HDTASTM D648204 °C
RTI StrUL 746140 °C
vicat--ISO 306/B120150 °C
Linear coefficient of thermal expansionTD：-40到40°CASTME8311.1E-04 cm/cm/°C
vicat--ISO 306/B50148 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8312.7E-05 cm/cm/°C
Heat distortion temperature1.8MPa,Unannealed,64.0mmSpan，HDTISO 75-2/Af155 °C
RTI ImpUL 746130 °C
Heat distortion temperature1.8MPa,未退火,3.20mm，HDTASTM D648163 °C
RTI ElecUL 746140 °C