PBT/PET

PBT/PET Pocan® ECOT3230 LANXESS GERMANY

393

Unit Price:US$ 2,444 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
28MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23℃23°C	ISO 180/1U	55 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30℃-30°C	ISO 180/1U	55 kJ/m²
Impact strength of cantilever beam gap	23℃23°C	ISO 180-1A	< 10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30℃-30°C	ISO 180-1A	< 10 kJ/m²
Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30℃-30°C	ISO 179/1eU	55 kJ/m²
Charpy Notched Impact Strength	23℃23°C	ISO 179/1eA	< 10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃-30°C	ISO 179/1eA	< 10 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
Bending strain			3 %
bending strength	23℃23℃4	ISO 178	230 Mpa
Bending modulus	23℃23℃4	ISO 178-A	10300 Mpa
Tensile strain	Break，23℃Break，23℃	ISO 527-2/5	2.8 %
tensile strength	Break，23℃Break，23℃	ISO 527-2/5	145 Mpa
Tensile modulus	23℃23℃	ISO 527-1-2	10400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	225 to 250 °C
Vicat softening temperature	B120B120	ISO 306/B120	205 °C
Linear coefficient of thermal expansion	TD：23~55℃TD：23 to 55℃	ISO 11359-2	0.000090 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23~55℃MD：23 to 55℃	ISO 11359-2	0.000030 1/℃

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium，23℃，50% RHEquilibrium，23℃，50% RH	ISO 62	0.1 %
Water absorption rate	Water absorption rate	Saturation，23℃Saturation，23℃	ISO 62	0.3 %
Shrinkage rate	MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.1 %
	Shrinkage rate	MD：270℃，2.0 mmFlow : 518°F, 0.0787 in 22	ISO 294-4	0.3 %
		Shrinkage rate	TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.2 %
		Shrinkage rate	Shrinkage rate	TD：270℃，2.0 mmAcross Flow : 518°F, 0.0787 in 22	ISO 294-4	0.9 %
Melt Volume Flow Rate (MVR)	260℃，5 kg260℃/5.0 kg	ISO 1133	30 cm3/10min
Apparent density		ISO 60	0.8 g/cm³
density	23°C	ISO 1183	1.55 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	Solution ASolution A	IEC 60112	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT/PET Pocan® ECOT3230 LANXESS GERMANY

Material Description

Technical Data Sheet Compare

Technical Data Sheet