PBT/PET ECOT3230 LANXESS GERMANY
Pocan®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS GERMANY/ECOT3230 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃23°C | ISO 179/1eA | < 10 kJ/m² |
| Impact strength of cantilever beam gap | 23℃23°C | ISO 180-1A | < 10 kJ/m² |
| Suspended wall beam without notch impact strength | -30℃-30°C | ISO 180/1U | 55 kJ/m² |
| Charpy Notched Impact Strength | -30℃-30°C | ISO 179/1eA | < 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30℃-30°C | ISO 179/1eU | 55 kJ/m² |
| Impact strength of cantilever beam gap | -30℃-30°C | ISO 180-1A | < 10 kJ/m² |
| Suspended wall beam without notch impact strength | 23℃23°C | ISO 180/1U | 55 kJ/m² |
| Impact strength of simply supported beam without notch | 23℃23°C | ISO 179/1eU | 65 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LANXESS GERMANY/ECOT3230 |
|---|---|---|---|
| Tensile strain | 断裂，23℃断裂，23℃ | ISO 527-2/5 | 2.8 % |
| Bending Strain | 3 % | ||
| bending strength | 23℃23℃4 | ISO 178 | 230 Mpa |
| tensile strength | 断裂，23℃断裂，23℃ | ISO 527-2/5 | 145 Mpa |
| Tensile modulus | 23℃23℃ | ISO 527-1-2 | 10400 Mpa |
| Flexural modulus | 23℃23℃4 | ISO 178-A | 10300 Mpa |
| Electrical performance | Test Condition | Test Method | LANXESS GERMANY/ECOT3230 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A解决方案 A | IEC 60112 | PLC 2 |
| physical property | Test Condition | Test Method | LANXESS GERMANY/ECOT3230 |
|---|---|---|---|
| Water absorption rate | 饱和，23℃饱和，23℃ | ISO 62 | 0.3 % |
| density | 23°C | ISO 1183 | 1.55 g/cm³ |
| Apparent density | ISO 60 | 0.8 g/cm³ | |
| Shrinkage rate | TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33 | ISO 294-4 | 0.2 % |
| Melt volume flow rate | 260℃，5 kg260℃/5.0 kg | ISO 1133 | 30 cm3/10min |
| Water absorption rate | 平衡，23℃，50% RH平衡，23℃，50% RH | ISO 62 | 0.1 % |
| Shrinkage rate | TD：270℃，2.0 mmAcross Flow : 518°F, 0.0787 in 22 | ISO 294-4 | 0.9 % |
| MD：270℃，2.0 mmFlow : 518°F, 0.0787 in 22 | ISO 294-4 | 0.3 % | |
| MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33 | ISO 294-4 | 0.1 % |
| Thermal performance | Test Condition | Test Method | LANXESS GERMANY/ECOT3230 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 225 to 250 °C | |
| Linear coefficient of thermal expansion | MD：23~55℃MD：23 到 55℃ | ISO 11359-2 | 0.000030 1/℃ |
| vicat | B120B120 | ISO 306/B120 | 205 °C |
| Linear coefficient of thermal expansion | TD：23~55℃TD：23 到 55℃ | ISO 11359-2 | 0.000090 1/℃ |