PC/PBT XENOY™  5720U-YW5E108 SABIC INNOVATIVE US

277
  • Unit Price:US$ 3,067 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    53MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Chemical resistance｜Low temperature impact resistance
  • Application Areas:Plastic bag｜Lighting applications｜Household daily necessities
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA47 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA55 kJ/m²
Dart impact-40°C, Energy at PeakASTM D376349.0 J
Dart impact-40°C, Total EnergyASTM D376359.0 J
Dart impact-30°C, Energy at PeakASTM D376349.0 J
Dart impact-30°C, Total EnergyASTM D376361.0 J
Dart impact-20°C, Energy at PeakASTM D376341.0 J
Dart impact-20°C, Total EnergyASTM D376353.0 J
Dart impact23°C, Energy at PeakASTM D376344.0 J
Dart impact23°C, Total EnergyASTM D376354.0 J
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6381830 Mpa
Tensile modulus--3Internal Method1830 Mpa
Tensile modulus--4ASTM D6381810 Mpa
Tensile modulus--ISO 527-2/11790 Mpa
tensile strengthYield5ASTM D63847.0 Mpa
tensile strengthYield6Internal Method45.0 Mpa
tensile strengthYield7ASTM D63844.0 Mpa
tensile strengthYieldISO 527-2/544.0 Mpa
tensile strengthYieldISO 527-2/5047.0 Mpa
tensile strengthBreak7ASTM D63850.0 Mpa
tensile strengthBreak6Internal Method47.0 Mpa
tensile strengthBreak5ASTM D63848.0 Mpa
tensile strengthBreakISO 527-2/543.0 Mpa
elongationYield7ASTM D6384.6 %
elongationYield6Internal Method4.6 %
elongationYield5ASTM D6384.0 %
elongationYieldISO 527-2/54.1 %
elongationYieldISO 527-2/504.6 %
elongationBreak7ASTM D638120 %
elongationBreak6Internal Method110 %
elongationBreak5ASTM D638120 %
elongationBreakISO 527-2/5110 %
elongationBreakISO 527-2/50120 %
Bending modulus50.0 mm Span8ASTM D7901660 Mpa
Bending modulus--9ISO 1781860 Mpa
bending strength--9,10ISO 17871.0 Mpa
bending strengthYield, 50.0 mm Span8ASTM D79070.0 Mpa
bending strengthBreak, 50.0 mm Span8ASTM D79069.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature110 °C
drying time4.0 to 6.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume50 to 80 %
Temperature at the rear of the barrel245 to 265 °C
Temperature in the middle of the barrel250 to 270 °C
Temperature at the front of the material cylinder255 to 275 °C
Spray nozzle temperature255 to 270 °C
Processing (melt) temperature260 to 275 °C
Mold temperature65 to 90 °C
Back pressure0.300 to 0.700 Mpa
Screw speed50 to 80 rpm
Exhaust hole depth0.013 to 0.020 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, Unannealed, 3.20 mmASTM D648108 °C
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648117 °C
Hot deformation temperature0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span12ISO 75-2/Bf109 °C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64883.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D64895.0 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span12ISO 75-2/Af87.0 °C
Vicat softening temperature--ASTM D152513119 °C
Vicat softening temperature--ISO 306/B120122 °C
Linear coefficient of thermal expansionFlow : -40 to 95°CASTM E8319.8E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : -30 to 80°CISO 11359-29.8E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8311.0E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -30 to 80°CISO 11359-21.0E-4 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Specific volumeASTM D7920.850 cm³/g
melt mass-flow rate250°C/2.16 kgASTM D12383.8 g/10 min
melt mass-flow rate250°C/5.0 kgASTM D123811 g/10 min
melt mass-flow rate265°C/2.16 kgASTM D12386.0 g/10 min
melt mass-flow rate266°C/5.0 kgASTM D123820 g/10 min
melt mass-flow rate250°C/2.16 kgISO 11333.0 g/10 min
Melt Volume Flow Rate (MVR)250°C/2.16 kgISO 11333.00 cm3/10min
Melt Volume Flow Rate (MVR)250°C/5.0 kgISO 113310.0 cm3/10min
Melt Volume Flow Rate (MVR)265°C/2.16 kgISO 11336.00 cm3/10min
Melt Volume Flow Rate (MVR)265°C/5.0 kgISO 113318.0 cm3/10min
Shrinkage rate3.20 mm，FlowInternal Method1.0 - 1.2 %
Water absorption rateSaturation, 23°CISO 620.28 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.080 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.