PA6

PA6 Amilan® CM1001G-20 TORAY JAPAN

628

Unit Price:US$ 2,533 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
100MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-40°C	kJ/m²	25
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	kJ/m²	55

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm		HB --

Basic Performance	Test Condition	Test Method	Test Result
Water absorption rate	24hr 23℃	ASTM D-570	1.3 %

mechanical properties	Test Condition	Test Method	Test Result
bending strength	-40°C	MPa	275 --
	bending strength	23°C	MPa	205 --
	bending strength	bending strength	80°C	MPa	115 --
Bending modulus	80°C	MPa	3200 2600
	Bending modulus	23°C	MPa	6800 3500
	Bending modulus	Bending modulus	-40°C	MPa	8700 7300
Tensile strain	Break,80°C	%	5.0 5.5
	Tensile strain	Break,23°C	%	3.0
	Tensile strain	Tensile strain	Break,-40°C	%	2.5 3.0
tensile strength	23°C	MPa	120 --
Compressive stress	-40°C	MPa	240 --
Bending modulus	23℃	ASTM D-790	60000 kg/cm
Izod Heng Strike	23℃ V-Notched1/2	ASTM D-256	6 kg·cm/cm
bending strength	-40℃	ASTM D-790	2400 kg/cm
Rockwell hardness	R-标度 23℃	ASTM D-785	120
Elongation at Break	23℃	ASTM D-638	5 %
Bending modulus	-40℃	ASTM D-790	78000 kg/cm
Rockwell hardness	M-标度 23℃	ASTM D-785	92
Tensile and flexural strength	23℃	ASTM D-638	1200 kg/cm
Bending modulus	80℃	ASTM D-790	29000 kg/cm
bending strength	23℃	ASTM D-790	1800 kg/cm
bending strength	bending strength	80℃	ASTM D-790	1000 kg/cm
Compressive stress	23°C	MPa	155 80.0
Compressive stress	Compressive stress	80°C	MPa	90.0 --
shear strength	23°C	MPa	115 65.0
Friction coefficient vs. Metal			0.15 --
Rockwell hardness		ASTM D785	R120.M92
Taber abraser	1000Cycles	mg	0.300 --

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		W/m/K	0.33 --
specific heat		J/kg/°C	1600 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	3E-05 --
Melting temperature		差示扫描测热计DSC	225 °C
Hot deformation temperature	18.6kg/cm	ASTM D-648	185 °C
specific heat			0.36 Cal/g·℃
Linear coefficient of thermal expansion		ASTM D-696	3
Hot deformation temperature	4.6kg/cm	ASTM D-648	215 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	°C	215 --
Melting temperature		°C	225 --
Melting temperature	Melting temperature			225 ℃（℉）

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	%	7.8 --
Water absorption rate	Water absorption rate	23°C,24hr	%	1.3 --
Shrinkage rate	MD:3.00mm4	%	0.30-0.50 --
Taber abraser	(1000g,CS-17)23 ℃	ASTM D-1044	12 mg/1000次
filler content			20 wt%
Shrinkage rate	TD:3.00mm3	%	0.60-0.90 --
Water absorption rate		ASTM D570/ISO 62	1.3 %
density		ASTM D792/ISO 1183	1.29

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	23°C,1kHz		0.040 --
Dissipation factor	Dissipation factor	23°C,50Hz		0.040 --
Dielectric constant	23°C,1MHz		3.80 --
	Dielectric constant	23°C,1kHz		4.40 --
	Dielectric constant	Dielectric constant	23°C,50Hz		4.60 --
Dielectric strength		kV/mm	20 --
Volume resistivity		ohms·cm	1E+15 1E+12
Volume resistivity	Volume resistivity		ASTM D257/IEC 60093	10^13 Ω.cm
Dielectric strength	1/8" 短时间	ASTM D-149	20 KV/mm
Volume resistivity		ASTM D-257	10 Ω·cm
Arc resistance		sec	120 --
Dissipation factor	23°C,1MHz		0.030 --

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Sale,23°C		120 --
	Rockwell hardness	R-Sale,80°C		12 --
	Rockwell hardness	Rockwell hardness	M-Sale,23°C		92 --

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Amilan® CM1001G-20 TORAY JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet