plas
Log In | Sign Up
CategoriesAll
Plastic Raw Materials
Modified Plastics
Plastic Additives
Color Masterbatch
Plastic Datasheets
Plastic News
About Us
Home
Plastic Raw Materials
ASA

ASA KIBILAC®  PW-957 TAIWAN CHIMEI

386
  • Unit Price:US$ 2,272 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    313MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:High gloss｜High mobility｜Weather resistance
  • Application Areas:Casters｜Fitness equipment｜Automotive sector｜Electrical appliances｜Electrical field｜Electronic field
  • Color:--
  • Grade:Extrusion grade

Material Certification

MSDS
RoHS
UL
TDS
TDS
UL
MSDS
RoHS
SVHC
Processing
Statement

Technical Data Sheet

flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.5mmUL 94HB
Basic PerformanceTest ConditionTest MethodTest Result
melt mass-flow rate220℃,10kgASTM D-123828 g/10min
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulusISO 1782200 Mpa
bending strengthASTM D79063.3 Mpa
bending strengthISO 17867.0 Mpa
tensile strengthYieldASTM D63843.0 Mpa
tensile strengthYieldISO 527-2/5046.0 Mpa
tensile strengthBreakISO 527-2/5033.0 Mpa
elongationBreakASTM D63855 %
Tensile strainBreakISO 527-2/5020 %
Bending modulusASTM D7902160 Mpa
tensile strengthASTM D-638420 kg/cm
bending strengthASTM D-790550 kg/cm
Impact strength of cantilever beam gap1/8"ASTM D-25615 kg.cm/cm
Impact strength of cantilever beam gapASTM D256/ISO 17910 kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gapASTM D256/ISO 17915 kg·cm/cm(J/M)ft·lb/in
tensile strengthASTM D638/ISO 527440 kg/cm²(MPa)[Lb/in²]
bending strengthASTM D790/ISO 178650 kg/cm²(MPa)[Lb/in²]
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A80.0 °C
Hot deformation temperature1.8MPa,AnnealedISO 75-2/A97.0 °C
Vicat softening temperatureASTM D15256105 °C
Vicat softening temperature--ISO 306/A50105 °C
Vicat softening temperature--ISO 306/B5094.0 °C
Linear coefficient of thermal expansionMDISO 11359-29E-05 cm/cm/°C
Hot deformation temperatureAnnealedASTM D64895 °C
Hot deformation temperatureUnannealedASTM D64885 °C
Vicat softening temperatureASTM D-1525105 °C
Hot deformation temperatureHDTASTM D648/ISO 7595 ℃（℉）
Hot deformation temperatureHDTASTM D648/ISO 7585 ℃（℉）
Vicat softening temperatureASTM D1525/ISO R306105 ℃（℉）
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate220°C/10.0kgASTM D123823 g/10min
Melt Volume Flow Rate (MVR)220°C/10.0kgISO 113323.0 cm3/10min
Shrinkage rateISO 294-40.40-0.70 %
densityASTM D792/ISO 11831.07
melt mass-flow rateASTM D1238/ISO 113328 g/10min
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785105
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.