Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA PW-957 TAIWAN CHIMEI
KIBILAC®
Casters、Fitness equipment、Automotive sector、Electrical appliances、Electrical field、Electronic field
High gloss、High mobility、Weather resistance
MSDS
RoHS
UL
TDS
TDS
UL
MSDS
RoHS
SVHC
Processing
Statement
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| Basic performance | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| melt mass-flow rate | 220℃,10kg | ASTM D-1238 | 28 g/10min |
| Mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 15 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 650 kg/cm²(MPa)[Lb/in²] | |
| ASTM D790 | 63.3 Mpa | ||
| Impact strength of cantilever beam gap | 1/8" | ASTM D-256 | 15 kg.cm/cm |
| Flexural modulus | ASTM D790 | 2160 Mpa | |
| tensile strength | ASTM D638/ISO 527 | 440 kg/cm²(MPa)[Lb/in²] | |
| 断裂 | ISO 527-2/50 | 33.0 Mpa | |
| 屈服 | ISO 527-2/50 | 46.0 Mpa | |
| elongation | 断裂 | ASTM D638 | 55 % |
| bending strength | ISO 178 | 67.0 Mpa | |
| Flexural modulus | ISO 178 | 2200 Mpa | |
| tensile strength | ASTM D-638 | 420 kg/cm | |
| 屈服 | ASTM D638 | 43.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| bending strength | ASTM D-790 | 550 kg/cm |
| Physical properties | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.07 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 28 g/10min |
| flammability | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 23 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 23.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PW-957 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 85 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 105 ℃（℉） | |
| ASTM D15256 | 105 °C | ||
| ASTM D-1525 | 105 °C | ||
| -- | ISO 306/A50 | 105 °C | |
| Heat distortion temperature | Unannealed，HDT | ASTM D648 | 85 °C |
| 1.8MPa,退火，HDT | ISO 75-2/A | 97.0 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C | |
| vicat | -- | ISO 306/B50 | 94.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 9E-05 cm/cm/°C |
| Heat distortion temperature | Annealed，HDT | ASTM D648 | 95 °C |