Material Description

Material Properties:High mobility｜Flame retardant
Application Areas:Home appliance components｜Fitness equipment｜Electronic field｜Electrical field
Color:--
Grade:High liquidity level

Material Certification

MSDS

RoHS

SGS

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	23 kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	210 J/m
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	180 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	9.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	22 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.0mm	UL 94	V-1
	UL flame retardant rating	1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	5VA

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2/50	37.0 Mpa
tensile strength	tensile strength	Break	ISO 527-2/50	28.0 Mpa
elongation	Break4	ASTM D638	15 %
elongation	elongation	Break	ISO 527-2/50	10 %
Bending modulus	--5	ASTM D790	2070 Mpa
Bending modulus	Bending modulus	--6	ISO 178	1800 Mpa
bending strength	--5	ASTM D790	60.7 Mpa
bending strength	bending strength	--6	ISO 178	55.0 Mpa
tensile strength	Yield4	ASTM D638	38.1 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	73.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	74.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ASTMD648	83.0 °C
Vicat softening temperature	--	ASTM D15257	90.0 °C
	Vicat softening temperature	--	ISO 306/A50	91.0 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	78.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.4E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
density	--3	ASTM D792	1.19 g/cm³
density	density	23°C	ISO 1183	1.19 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	5.0 g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	50.0 cm3/10min
Shrinkage rate		ISO 294-4	0.30-0.60 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.