ABS PA-765 TAIWAN CHIMEI
POLYLAC® 
Home appliance components、Fitness equipment、Electronic field、Electrical field
High mobility、Flame retardant
MSDS
RoHS
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTAIWAN CHIMEI/PA-765
Impact strength of cantilever beam gap-30°CISO180/1A9.0 kJ/m²
23°C,3.20mmASTMD256210 J/m
23°CISO180/1A22 kJ/m²
Charpy Notched Impact Strength-30°CISO17910 kJ/m²
Impact strength of cantilever beam gap23°C,6.40mmASTMD256180 J/m
Charpy Notched Impact Strength23°CISO17923 kJ/m²
hardnessTest ConditionTest MethodTAIWAN CHIMEI/PA-765
Rockwell hardnessR级ASTMD785100
Mechanical propertiesTest ConditionTest MethodTAIWAN CHIMEI/PA-765
tensile strength屈服ISO527-2/5037.0 Mpa
屈服4ASTMD63838.1 Mpa
断裂ISO527-2/5028.0 Mpa
elongation断裂4ASTMD63815 %
Flexural modulus--5ASTMD7902070 Mpa
bending strength--5ASTMD79060.7 Mpa
elongation断裂ISO527-2/5010 %
bending strength--6ISO17855.0 Mpa
Flexural modulus--6ISO1781800 Mpa
flammabilityTest ConditionTest MethodTAIWAN CHIMEI/PA-765
UL flame retardant rating1.5mmUL94V-0
1.0mmUL94V-1
2.5mmUL945VA
physical property Test ConditionTest MethodTAIWAN CHIMEI/PA-765
density23°CISO11831.19 g/cm³
melt mass-flow rate200°C/5.0kgASTMD12385.0 g/10min
density--3ASTMD7921.19 g/cm³
Melt volume flow rate220°C/10.0kgISO113350.0 cm3/10min
Shrinkage rateISO294-40.30到0.60 %
Thermal performanceTest ConditionTest MethodTAIWAN CHIMEI/PA-765
1.8MPa,退火ASTMD648,ISO75-2/A83.0 °C
1.8MPa,未退火ISO75-2/A74.0 °C
vicat--ISO306/A5091.0 °C
--ASTMD1525790.0 °C
MDISO11359-28.4E-05 cm/cm/°C
vicat--ISO306/B5078.0 °C
1.8MPa,未退火ASTMD64873.0 °C