PA66 Zytel® 80G43GS1L BK104 DUPONT USA
159
- Unit Price:US$ 5,834 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:28MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜high strength｜Filler: Glass fiber reinforced material｜43% filler by weight
- Application Areas:Fitness equipment｜Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 262 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 261 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 250 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| FMVSS flammability | FMVSS302 | B |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 78 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MediumDensity | 1.27 g/cm³ | ||
| Ejection Temperature | 195 °C | ||
| SpecificHeatCapacity of Melt | 2050 J/kg/°C | ||
| ThermalConductivityofMelt | 0.25 W/m/K | ||
| shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 4.9 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.5 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
| flexural modulus | ISO 178 | 10300 Mpa | |
| Tensile modulus | ISO 527-2 | 11700 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 169 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.