Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 80G43GS1L BK104 DUPONT USA
Zytel®
Fitness equipment,Automotive Applications
Glass fiber reinforced,high strength,Filler: Glass fiber reinf,43% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/80G43GS1L BK104 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 78 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| thermal performance | Test Condition | Test Method | DUPONT USA/80G43GS1L BK104 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 250 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 261 °C | |
| vicat | ISO 306/B50 | 215 °C | |
| melting temperature | ISO 11357-3 | 262 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/80G43GS1L BK104 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11700 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 3.3 % |
| tensile strength | 断裂 | ISO 527-2 | 169 Mpa |
| flexural modulus | ISO 178 | 10300 Mpa |
| Physical properties | Test Condition | Test Method | DUPONT USA/80G43GS1L BK104 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 1.5 % |
| ThermalConductivityofMelt | 0.25 W/m/K | ||
| SpecificHeatCapacity of Melt | 2050 J/kg/°C | ||
| shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MediumDensity | 1.27 g/cm³ | ||
| Ejection Temperature | 195 °C | ||
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 4.9 % |
| shrinkage rate | MD | ISO 294-4 | 0.20 % |
| flammability | Test Condition | Test Method | DUPONT USA/80G43GS1L BK104 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |