Plastic Raw Materials
PA612

PA612 SC315 NC010 DUPONT USA

257
  • Unit Price:US$ 6,283 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    25MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:--
  • Application Areas:--
  • Color:--
  • Grade:--

Technical Data Sheet

Filling analysisTest ConditionTest MethodTest Result
Melt density0.900 g/cm³
Specific Heat Capacity of Melt2750 J/kg/°C
Thermal Conductivity of Melt0.18 W/m/K
Emission of Organic CompoundsVDA 2773.10 µgC/g
impact performanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
flammabilityTest ConditionTest MethodTest Result
Extreme Oxygen IndexISO 4589-227 %
squeeze outTest ConditionTest MethodTest Result
drying temperature80 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.060 %
Melt Temperature235 to 250 °C
Extrusion Melt Temperature, Optimum240 °C
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulusISO 527-22400 Mpa
tensile strengthYieldISO 527-262.0 Mpa
Tensile strainYieldISO 527-24.5 %
Nominal tensile fracture strainISO 527-217 %
Bending modulusISO 1782100 Mpa
injectionTest ConditionTest MethodTest Result
Drying time - hot air dryer2.0 to 4.0 hr
Suggested maximum moisture content0.15 %
Processing (melt) temperature230 to 290 °C
Melt Temperature, Optimum250 °C
Mold temperature50 to 90 °C
Mold Temperature, Optimum70 °C
Maintain pressure50.0 to 100 Mpa
Maintain pressureDrying Recommendedyes
Hold Pressure Time4.00 s/mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B135 °C
Hot deformation temperature1.8 MPa, UnannealedISO 75-2/A62.0 °C
Vicat softening temperatureISO 306/B50181 °C
Melting temperatureISO 11357-3218 °C
Linear coefficient of thermal expansionFlowISO 11359-21.1E-4 cm/cm/°C
Linear coefficient of thermal expansionFlow : -40 to 23°CISO 11359-29.0E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 55 to 160°CISO 11359-21.6E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross FlowISO 11359-21.2E-4 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 23°CISO 11359-29.0E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 55 to 160°CISO 11359-21.8E-4 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
Shrinkage rate横向FlowISO 294-41.4 %
Shrinkage rateFlowISO 294-41.3 %
Water absorption rateSaturation, 23°C, 2.00 mmISO 623.0 %
Water absorption rateEquilibrium, 23°C, 2.00 mm, 50% RHISO 621.3 %
Stickiness96% H2SO4ISO 30795.0 cm³/g
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityIEC 62631-3-11.0E+13 ohms·m
Dielectric strengthIEC 60243-130 KV/mm
Relative permittivity1 MHzIEC 62631-2-13.20
Relative permittivity100 HzIEC 62631-2-13.60
Dissipation factor100 HzIEC 62631-2-10.014
Dissipation factor1 MHzIEC 62631-2-10.016
Compared to the anti leakage trace indexIEC 60112 V
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR -SaleISO 2039-2114
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.