ABS Novodur® H801 INEOS USA
253
- Unit Price:US$ 3,937 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:26MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜heat-resisting
- Application Areas:Home appliance components｜Automotive sector｜Automotive interior parts｜Application in the automotive field｜Automotive interior equipment
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Pressure Test | ISO 2039-1 | 105 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO 75-2/Bf | 106 °C |
| 1.80MPaAnnealed | ISO 75-2/Af | 99 °C | |
| Vicat softening temperature | 5.10kg | ISO 306/A50 | 105 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melting temperature | ISO 294 | 240 °C | |
| Injection speed | ISO 294 | 240 mm/sec | |
| Burning rate | ISO 3795 | 45 mm/min |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ignition temperature of heating wire | 2.00mm | IEC 60695-2-12 | 700 °C |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.07 g/cm³ | |
| melt mass-flow rate | 220℃/10.0Kg | ISO 1133 | 9 g/10min |
| 线性收缩率 | ISO 294-4 | 0.5-0.7 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm | |
| Surface resistivity | IEC 60093 | 1E+16 Ω.cm | |
| Dielectric strength | 1.00mm | IEC 60243-1 | 38 KV/mm |
| Dielectric constant | IEC 60250 | 3 1MHz | |
| IEC 60250 | 3.1 100HZ | ||
| Dissipation factor | IEC 60250 | 0.05 | |
| IEC 60250 | 0.09 | ||
| 相对漏电起痕指数 | IEC 60112 | 600 V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Bending modulus | 23°C | ISO 178 | 2300 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| -30°C | ISO 179/1eA | 12 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 220 kJ/m² |
| -30°C | ISO 179/1eU | 160 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 30 kJ/m² |
| -30°C | ISO 180/1A | 12 kJ/m² | |
| tensile strength | Yield，23°C | ISO 527-2 | 49 Mpa |
| Elongation at Break | Yield，23°C | ISO 527-2 | 3 % |
| 23°C | ISO 527-2 | >=15 % | |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| bending strength | 23°C | ISO 178 | 77 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.