ABS H801 INEOS USA
Novodur®
Home appliance components、Automotive sector、Automotive interior parts、Application in the automo、Automotive interior equip
UV resistance、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| melting temperature | ISO 294 | 240 °C | |
| burning rate | ISO 3795 | 45 mm/min | |
| injection speed | ISO 294 | 240 mm/sec |
| hardness | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 105 Mpa |
| Mechanical properties | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| bending strength | 23°C | ISO 178 | 77 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 30 kJ/m² |
| Flexural modulus | 23°C | ISO 178 | 2300 Mpa |
| elongation at break | 屈服，23°C | ISO 527-2 | 3 % |
| tensile strength | 屈服，23°C | ISO 527-2 | 49 Mpa |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 160 kJ/m² |
| Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
| elongation at break | 23°C | ISO 527-2 | >=15 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 220 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
| Electrical performance | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 0.09 | |
| dielectric strength | 1.00mm | IEC 60243-1 | 38 KV/mm |
| dielectric constant | IEC 60250 | 3.1 100HZ | |
| Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
| dielectric constant | IEC 60250 | 3 1MHz | |
| Surface Resistivity | IEC 60093 | 1E+16 Ω.cm | |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| GWIT | 2.00mm | IEC 60695-2-12 | 700 °C |
| physical property | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| melt mass-flow rate | 线性收缩率 | ISO 294-4 | 0.5-0.7 % |
| density | ISO 1183 | 1.07 g/cm³ | |
| melt mass-flow rate | 220℃/10.0Kg | ISO 1133 | 9 g/10min |
| Thermal performance | Test Condition | Test Method | INEOS USA/H801 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 99 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 106 °C |
| vicat | 5.10kg | ISO 306/A50 | 105 °C |