PEI EXTEM™ VH1003-1000 SABIC INNOVATIVE US

250
  • Unit Price:US$ 21,366 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    30.1MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Chemical resistance｜heat-resisting｜Flame retardant｜high strength
  • Application Areas:Automotive sector｜aviation industry
  • Color:--
  • Grade:--

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
transmissivity2540μmASTM D100358.0 %
turbidity2540μmASTM D10032.0 %
impact performanceTest ConditionTest MethodTest Result
Dart impact23°C,TotalEnergyASTM D376333.9 J
-30°CISO 180/1U无断裂
23°CASTMD4812无断裂
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
-30°CASTM D25674 J/m
23°CASTM D25669 J/m
-30°CISO 180/1A5.4 kJ/m²
23°CISO 180/1A4.6 kJ/m²
flammabilityTest ConditionTest MethodTest Result
Burning wire flammability index3.20mmIEC 60695-2-12960 °C
Hot filament ignition temperature3.00mmIEC 60695-2-13850 °C
Extreme Oxygen IndexISO 4589-245 %
mechanical propertiesTest ConditionTest MethodTest Result
crackASTM D63850 %
crackISO 527-2/517 %
50.0mm spanASTM D7903170 Mpa
yieldISO 527-2/58.5 %
yieldASTM D6386.0 %
crackISO 527-2/578.0 Mpa
crackASTM D63896.5 Mpa
yieldISO 527-2/595.0 Mpa
yieldASTM D63896.5 Mpa
--8ISO 1783080 Mpa
--9ISO 178123 Mpa
Yield, 100mm spanASTM D790155 Mpa
Fracture, 50.0mm spanASTM D790159 Mpa
--2ASTM D6383520 Mpa
thermal performanceTest ConditionTest MethodTest Result
Ball Pressure Test125°CIEC 60695-10-2Pass
1.8MPa, unannealed, 64.0mm span ofISO 75-2/Af228 °C
1.8MPa, unannealed, 6.40mmASTM D648230 °C
1.8MPa, unannealed, 3.20mmASTM D648217 °C
0.45MPa, unannealed, 6.40mmASTM D648237 °C
thermal conductivityASTME15300.22 W/m/K
Horizontal: 23 to 150 ° CAcross Flow, 23to150℃ISO 11359-25E-05 cm/cm/°C
Horizontal: -40 to 150 ° CAcross Flow, -40to150°CASTME8315E-05 cm/cm/°C
Flow: 23 to 150 ° C23to150℃ISO 11359-25E-05 cm/cm/°C
Flow: -40 to 150 ° C-40to150°CASTME8315E-05 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate367°C/6.6kgASTM D123816 g/10min
Melt Volume Flow Rate (MVR)360°C/5.0kgISO 11338.50 cm3/10min
Shrinkage rateMD1Internal Method0.50-0.70 %
Shrinkage rateMD:3.20mmInternal Method0.50-0.70 %
Shrinkage rateTD:3.20mmInternal Method0.50-0.70 %
Water absorption rateSaturation,23°CISO 621.8 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.60 %
Electrical performanceTest ConditionTest MethodTest Result
Dissipation factor60HzIEC 602500.025
Dissipation factor50HzIEC 602500.025
Dielectric constant1kHzASTM D1503.41
Dielectric constant100HzASTM D1503.41
Dielectric strength3.20mm,inOilASTM D14917 KV/mm
Dissipation factor100HzIEC 602508E-03
Dissipation factor1kHzIEC 602501E-03
Dissipation factor1MHzIEC 602507E-03
Compared to the anti leakage trace indexIEC 60112PLC 3
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestH358/30ISO 2039-1141 Mpa
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.