PC CH8105 1002 B CANGZHOU DAHUA

207

Unit Price:US$ 1,688 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
50MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
transmissivity		ISO 13468	89 %
Cleanliness	2000?	ISO 14782	0.8 %
Refractive index		ISO 489	1.586

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	1.0mm/min	ISO 527	2400 Mpa
tensile strength	Yield50mm/min	ISO 527	60 Mpa
elongation	Yield50mm/min	ISO 527	6 %
elongation	elongation	Break50mm/mi	ISO 527	150 %
bending strength	Yield2.0mm/min	ISO 178	97 Mpa
Bending modulus	2.0mm/min	ISO 178	2410 Mpa
Impact strength of cantilever beam gap	23℃	ISO 180	70 kJ/㎡
Suspended wall beam without notch impact strength	23℃	ISO 180	NB kJ/㎡
Charpy Notched Impact Strength	23℃	ISO 179	75 kJ/㎡
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	NB kJ/㎡

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	Annealed0.45MPa	ISO 75	144 °C
Hot deformation temperature	Hot deformation temperature	Unannealed1.8MPa	ISO 75	128 °C
Vicat softening temperature	50℃/hr 50N	ISO 306	149 °C
Glass transition temperature	10℃/min	ISO 11357	149 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.2 g/cm³
Shrinkage rate	Flow2.0mm	ISO 294	0.50-0.70 %
Shrinkage rate	Shrinkage rate	垂直2.0mm	ISO 294	0.50-0.70 %
Water absorption rate	23°C24hr	ISO 62	0.32 %
Water absorption rate	Water absorption rate	23℃ 50RH	ISO 62	0.15 %
melt mass-flow rate	300°C 1.2kg	ISO 1133	10 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	2.0mm	IEC 60093	200000000000000000 Ω.cm
Surface resistivity	2.0mm	IEC 60093	10000000000000000 Ω
Dielectric strength	1.0mm	IEC 60243	34 KV/mm
Dielectric constant	100Hz	IEC 60250	3.1
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3
Dissipation factor	100Hz	IEC 60250	0.001
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.01
Anti leakage trace index		IEC 60112	250 V

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039	120

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Ignition temperature of heating wire	1.5mm	IEC 60695	875 °C
Ignition temperature of heating wire	Ignition temperature of heating wire	3mm	IEC 60695	875 °C
Relative temperature of heating wire	1.5mm	IEC 60695	875 °C
Relative temperature of heating wire	Relative temperature of heating wire	3mm	IEC 60695	960 °C
Extreme Oxygen Index		ISO 4589	27 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.