Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC CH8105 1002 B CANGZHOU DAHUA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
Rockwell hardnessISO 2039120
Mechanical propertiesTest ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
Tensile modulus1.0mm/minISO 5272400 Mpa
Charpy Notched Impact Strength23℃ISO 179NB kJ/㎡
elongation断裂50mm/miISO 527150 %
Suspended wall beam without notch impact strength23℃ISO 180NB kJ/㎡
elongation屈服50mm/minISO 5276 %
bending strength屈服2.0mm/minISO 17897 Mpa
Flexural modulus2.0mm/minISO 1782410 Mpa
tensile strength 屈服50mm/minISO 52760 Mpa
Impact strength of cantilever beam gap23℃ISO 18070 kJ/㎡
Electrical performanceTest ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
Volume resistivity2.0mmIEC 60093200000000000000000 Ω.cm
Surface Resistivity2.0mmIEC 6009310000000000000000 Ω
dielectric constant100HzIEC 602503.1
proof tracking indexIEC 60112250 V
Dissipation Factor100HzIEC 602500.001
dielectric strength1.0mmIEC 6024334 KV/mm
dielectric constant1MHzIEC 602503
Dissipation Factor1MHzIEC 602500.01
optical performance Test ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
cleanliness2000㎛ISO 147820.8 %
transmissivityISO 1346889 %
refractive indexISO 4891.586
Flame retardant performanceTest ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
GWIT1.5mmIEC 60695875 °C
Relative temperature of heating wire3mmIEC 60695960 °C
1.5mmIEC 60695875 °C
GWIT3mmIEC 60695875 °C
UL flame retardant rating3.0mmUL 94HB
Limiting Oxygen IndexISO 458927 %
UL flame retardant rating1.5mmUL 94HB
physical property Test ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
Water absorption rate23℃ 50RHISO 620.15 %
23°C24hrISO 620.32 %
melt mass-flow rate300°C 1.2kgISO 113310 g/10min
Shrinkage rate垂直2.0mmISO 2940.50-0.70 %
流动2.0mmISO 2940.50-0.70 %
densityISO 11831.2 g/cm³
Thermal performanceTest ConditionTest MethodCANGZHOU DAHUA/CH8105 1002 B
Heat distortion temperature退火0.45MPa，HDTISO 75144 °C
Glass Transition Temperature10℃/minISO 11357149 °C
vicat50℃/hr 50NISO 306149 °C
Heat distortion temperature未退火1.8MPa，HDTISO 75128 °C