PA66 LNP™ THERMOCOMP™ RB004 SABIC INNOVATIVE US
210
- Unit Price:US$ 3,912 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜High temperature resistance｜Filler: Glass beads
- Application Areas:Automotive components｜Sports equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 233 °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 219 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 81.0 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 77.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 7.3E-05 cm/cm/°C |
| TD：-30to30°C | ASTM D696 | 7.1E-05 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.1 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 17 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 2.70 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 0.820 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：24小时 | ASTM D955 | 1.0-3.0 % |
| TD：24hr | ASTM D955 | 1.0-3.0 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.62 % |
| 平衡,23°C,50%RH | ISO 62 | 1.1 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 4100 Mpa | |
| ISO 527-2/1 | 3970 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/5 | 79.0 Mpa |
| 断裂 | ASTM D638 | 80.0 Mpa | |
| 断裂 | ISO 527-2/5 | 75.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.8 % |
| elongation | 断裂 | ASTM D638 | 3.7 % |
| Tensile strain | 断裂 | ISO 527-2/5 | 3.9 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 3870 Mpa |
| ISO 178 | 3710 Mpa | ||
| bending strength | ISO 178 | 119 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.