PA66 RB004 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Automotive components,Sports equipment
Thermal stability,High temperature resistan,Filler: Glass beads
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/RB004 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 2.70 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.1 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 0.820 J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 17 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/RB004 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 219 °C |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 233 °C | |
| 1.8MPa,未退火,3.20mm | ASTM D648 | 81.0 °C | |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 77.0 °C | |
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTM D696 | 7.1E-05 cm/cm/°C |
| MD：-30到30°C | ASTM D696 | 7.3E-05 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RB004 |
|---|---|---|---|
| bending strength | ISO 178 | 119 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.7 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 3870 Mpa |
| ISO 178 | 3710 Mpa | ||
| Tensile modulus | ISO 527-2/1 | 3970 Mpa | |
| ASTM D638 | 4100 Mpa | ||
| Tensile strain | 断裂 | ISO 527-2/5 | 3.9 % |
| 屈服 | ISO 527-2/5 | 3.8 % | |
| tensile strength | 断裂 | ISO 527-2/5 | 75.0 Mpa |
| 断裂 | ASTM D638 | 80.0 Mpa | |
| 屈服 | ISO 527-2/5 | 79.0 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/RB004 |
|---|---|---|---|
| shrinkage rate | MD：24小时 | ASTM D955 | 1.0-3.0 % |
| TD：24hr | ASTM D955 | 1.0-3.0 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.62 % |
| 平衡,23°C,50%RH | ISO 62 | 1.1 % |