PBT VALOX™ Resin 420-7001 SABIC INNOVATIVE US
207
- Unit Price:US$ 3,273 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| R级 | ISO 2039-2 | 118 | |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 122 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 216 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Imp | UL 746 | 140 °C | |
| vicat | -- | ISO 306/A50 | 223 °C |
| -- | ISO 306/B50 | 215 °C | |
| thermal conductivity | ISO 8302 | 0.19 W/m/K | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 203 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| vicat | ASTM D152514 | 215 °C | |
| -- | ISO 306/B120 | 215 °C | |
| RTI Elec | UL 746 | 140 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 207 °C |
| Linear coefficient of thermal expansion | MD：60to138°C | ASTME831 | 2.5E-05 cm/cm/°C |
| MD：-40to40°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 220 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 204 °C |
| RTI Str | UL 746 | 140 °C | |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 217 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 750 °C |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 19 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler | ASTM D229 | 30 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 45 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：--4 | 内部方法 | 0.50-0.80 % |
| MD：--2 | 内部方法 | 0.30-0.70 % | |
| MD：3.20mm | 内部方法 | 0.30-0.80 % | |
| Specific volume | ASTM D792 | 0.660 cm³/g | |
| shrinkage rate | TD：--3 | 内部方法 | 0.40-0.60 % |
| MD：--3 | 内部方法 | 0.30-0.50 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| shrinkage rate | TD：--2 | 内部方法 | 0.50-1.0 % |
| Water absorption rate | 24hr | ASTM D570 | 0.090 % |
| shrinkage rate | TD：--5 | 内部方法 | 0.60-0.90 % |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 17 g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
| shrinkage rate | TD：3.20mm | 内部方法 | 0.50-1.0 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | 1.00mm15 | IEC 60243-1 | 19 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.10 |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 25 KV/mm |
| 0.800mm,在油中 | IEC 60243-1 | 28 KV/mm | |
| relative permittivity | 50Hz | IEC 60250 | 3.10 |
| volume resistivity | ASTM D257 | >3.2E+16 ohms·cm | |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| 1MHz | IEC 60250 | 0.010 | |
| arc resistance | ASTM D495 | PLC 5 | |
| Dissipation Factor | 100Hz | IEC 60250 | 1E-03 |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 24 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| Dissipation Factor | 60Hz | IEC 60250 | 1E-03 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| dielectric constant | 100Hz | ASTM D150 | 3.80 |
| relative permittivity | 60Hz | IEC 60250 | 3.10 |
| Dissipation Factor | 50Hz | IEC 60250 | 1E-03 |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield | ASTM D638 | 120 Mpa |
| Tensile modulus | ISO 527-2/1 | 9300 Mpa | |
| Tensile strain | Yield | ASTM D638 | 2.7 % |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 195 Mpa |
| Break,50.0mmSpan | ASTM D790 | 190 Mpa | |
| ISO 178 | 195 Mpa | ||
| flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.0 % |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 19.0 mg |
| tensile strength | Break | ASTM D638 | 120 Mpa |
| Tensile modulus | ASTM D638 | 9300 Mpa | |
| Tensile strain | Break | ASTM D638 | 2.7 % |
| tensile strength | 断裂 | ISO 527-2/5 | 125 Mpa |
| flexural modulus | 50.0mmSpan | ASTM D790 | 7580 Mpa |
| tensile strength | 屈服 | ISO 527-2/5 | 125 Mpa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.