PBT 420-7001 SABIC INNOVATIVE US
VALOX™ Resin
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 45 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 45 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 122 Mpa |
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Supplementary Information | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| filler | ASTM D229 | 30 % |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 9300 Mpa | |
| tensile strength | Yield | ASTM D638 | 120 Mpa |
| 断裂 | ISO 527-2/5 | 125 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.0 % |
| bending strength | Break,50.0mmSpan | ASTM D790 | 190 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 19.0 mg |
| Flexural modulus | 50.0mmSpan | ASTM D790 | 7580 Mpa |
| Tensile strain | Break | ASTM D638 | 2.7 % |
| tensile strength | 屈服 | ISO 527-2/5 | 125 Mpa |
| Tensile modulus | ASTM D638 | 9300 Mpa | |
| bending strength | Yield,50.0mmSpan | ASTM D790 | 195 Mpa |
| tensile strength | Break | ASTM D638 | 120 Mpa |
| Tensile strain | Yield | ASTM D638 | 2.7 % |
| bending strength | ISO 178 | 195 Mpa | |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.0 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| relative permittivity | 60Hz | IEC 60250 | 3.10 |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 28 KV/mm |
| relative permittivity | 50Hz | IEC 60250 | 3.10 |
| Volume resistivity | ASTM D257 | >3.2E+16 ohms·cm | |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| 1MHz | ASTM D150 | 0.020 | |
| 100Hz | IEC 60250 | 1E-03 | |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 16 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.10 |
| dielectric constant | 100Hz | ASTM D150 | 3.80 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010 |
| 60Hz | IEC 60250 | 1E-03 | |
| 50Hz | IEC 60250 | 1E-03 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| dielectric strength | 1.00mm15 | IEC 60243-1 | 19 KV/mm |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric strength | 1.60mm,在油中 | IEC 60243-1 | 24 KV/mm |
| 3.20mm,inAir | ASTM D149 | 19 KV/mm | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 25 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 750 °C |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Limiting Oxygen Index | ASTM D2863 | 19 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30-0.80 % |
| melt mass-flow rate | 250°C/2.16kg | ISO 1133 | 17 g/10min |
| Water absorption rate | 24hr | ASTM D570 | 0.090 % |
| 平衡,23°C,50%RH | ISO 62 | 0.080 % | |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.50-1.0 % |
| MD：--2 | 内部方法 | 0.30-0.70 % | |
| MD：--3 | 内部方法 | 0.30-0.50 % | |
| MD：--4 | 内部方法 | 0.50-0.80 % | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
| Shrinkage rate | TD：--2 | 内部方法 | 0.50-1.0 % |
| TD：--3 | 内部方法 | 0.40-0.60 % | |
| TD：--5 | 内部方法 | 0.60-0.90 % | |
| Specific volume | ASTM D792 | 0.660 cm³/g |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/420-7001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 207 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| MD：60to138°C | ASTME831 | 2.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 220 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 216 °C |
| RTI Str | UL 746 | 140 °C | |
| Heat distortion temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 217 °C |
| thermal conductivity | ISO 8302 | 0.19 W/m/K | |
| vicat | -- | ISO 306/B120 | 215 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| vicat | -- | ISO 306/A50 | 223 °C |
| ASTM D152514 | 215 °C | ||
| -- | ISO 306/B50 | 215 °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 140 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Af | 204 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 203 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| RTI Elec | UL 746 | 140 °C |