PA6/66 Ultramid® C3U BK BASF GERMANY

373

Unit Price:US$ 10,586 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜Flame retardant
Application Areas:Electronic insulation｜Electrical components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.16 g/cm³
density	density		ISO 1183	1.16 g/cm³
Melt volume flow rate		ISO 1133	140 cm3/10min
Shrinkage rate			0.80 %
Water absorption rate		ASTM D570	8.5 %
	Water absorption rate		ISO 62	8.5 %
		Water absorption rate		ASTM D570	2.9 %
		Water absorption rate	Water absorption rate		ISO 62	2.9 %

hardness	Test Condition	Test Method	Test Result
ball-indentation hardness		ISO 2039-1	100 Mpa

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
	UL flame retardant rating		UL 94	V-0
		UL flame retardant rating		UL 94	V-0
		UL flame retardant rating	UL flame retardant rating		UL 94	V-0

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ISO 527-2	75.0 Mpa
elongation		ASTM D638	5.0 %
Tensile strain		ISO 527-2	4.0 %
elongation		ASTM D638	50 %
Nominal tensile fracture strain		ISO 527-2	6.0 %
Flexural modulus		ASTM D790	3000 Mpa
Flexural modulus	Flexural modulus		ISO 178	3000 Mpa
Tensile modulus		ISO 527-2	3500 Mpa
tensile strength		ASTM D638	83.0 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO 179	9.0 kJ/m²
Impact strength of simply supported beam without notch		ISO 179	80 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	32 J/m
	Impact strength of cantilever beam gap		ASTM D256	43 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	4.5 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	1E+13 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	1E+13 ohms·cm
dielectric strength		IEC 60243-1	32 KV/mm
dielectric constant		IEC 60250	3.60
Dissipation Factor		IEC 60250	0.020
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion			8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion			9E-05 cm/cm/°C
RTI Elec		UL 746	110 °C
	RTI Elec		UL 746	120 °C
		RTI Elec		UL 746	120 °C
		RTI Elec	RTI Elec		UL 746	120 °C
RTI Imp		UL 746	65.0 °C
	RTI Imp		UL 746	105 °C
		RTI Imp		UL 746	105 °C
		RTI Imp	RTI Imp		UL 746	105 °C
Heat distortion temperature		ASTM D648	224 °C
	Heat distortion temperature		ASTM D648	91.0 °C
	Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	70.0 °C
melting temperature		ASTM D3418	243 °C
melting temperature	melting temperature		ISO 3146	243 °C
Linear coefficient of thermal expansion		ASTME831	4E-05 cm/cm/°C
RTI Str		UL 746	65.0 °C
	RTI Str		UL 746	115 °C
		RTI Str		UL 746	120 °C
		RTI Str	RTI Str		UL 746	120 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.