PBT VALOX™ VX5011 SABIC INNOVATIVE US
146
- Unit Price:US$ 2,307 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:45MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low warpage｜Aging resistance｜Filler: Glass fiber reinforced material｜10% filler by weight
- Application Areas:chip｜Electronic and Electrical Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 50.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.50-0.90 % | |
| Water absorption rate | ISO 62 | 0.15 % | |
| ISO 62 | 0.10 % | ||
| Melt volume flow rate | ISO 1133 | 75.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.30-0.80 % | |
| 内部方法 | 0.40-0.60 % | ||
| Melt volume flow rate | ISO 1133 | 18.0 cm3/10min | |
| melt mass-flow rate | ASTM D1238 | 85 g/10min | |
| ASTM D1238 | 85 g/10min | ||
| density | ASTMD792 | 1.31 g/cm³ | |
| melt mass-flow rate | ASTM D1238 | 18 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 165 Mpa | |
| Rockwell hardness | ISO 2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 750 °C | |
| IEC 60695-2-12 | 850 °C | ||
| Limiting Oxygen Index | ISO 4589-2 | 21 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| filler | ASTM D229 | 10 % |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt viscosity | ISO 11443 | 145 Pa·s |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| -30°C | ISO 180/1A | 5.0 kJ/m² | |
| 0°C | ASTM D256 | 47 J/m | |
| 23°C | ASTM D256 | 47 J/m | |
| -30°C | ASTM D256 | 47 J/m | |
| 23°C | ISO 179/1eU | 40 kJ/m² | |
| -30°C | ISO 179/2U | 40 kJ/m² | |
| ISO 179/1eU | 30 kJ/m² | ||
| 23°C | ISO 179/2C | 6.0 kJ/m² | |
| ISO 179/1eA | 4.0 kJ/m² | ||
| -30°C | ISO 179/2C | 6.0 kJ/m² | |
| ISO 179/1eA | 4.0 kJ/m² | ||
| 0°C | ISO 180/1A | 5.0 kJ/m² | |
| 23°C | ISO 180/1A | 6.0 kJ/m² | |
| -30°C | ASTM D4812 | 470 J/m | |
| 23°C | ASTM D4812 | 480 J/m | |
| -30°C | ISO 180/1U | 30 kJ/m² | |
| 23°C | ISO 180/1U | 40 kJ/m² | |
| Dart impact | ASTM D3763 | 37.0 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| yield | ISO 527-2/5 | 3.0 % | |
| ASTM D638 | 3.0 % | ||
| fracture | ISO 527-2/5 | 95.0 Mpa | |
| yield | ISO 527-2/5 | 95.0 Mpa | |
| fracture | ASTM D638 | 90.0 Mpa | |
| --3 | ASTM D638 | 4600 Mpa | |
| yield | ASTM D638 | 90.0 Mpa | |
| Fracture bending strain | ISO 178 | 5.0 % | |
| fracture | ASTM D638 | 3.0 % | |
| ISO 527-2/5 | 3.0 % | ||
| 50.0mm span | ASTM D790 | 3600 Mpa | |
| --9 | ISO 178 | 4000 Mpa | |
| --10 | ISO 178 | 140 Mpa | |
| --11 | ISO 178 | 130 Mpa | |
| Yield, 50.0mm span | ASTM D790 | 126 Mpa | |
| Taber abraser | 内部方法 | 54.0 mg |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1MHz | ASTMD150 | 3.10 | |
| ASTMD150 | 0.014 | ||
| 100Hz | IEC 60250 | 3.20 | |
| 60Hz | IEC 60250 | 3.00 | |
| 50Hz | IEC 60250 | 3.00 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 | |
| IEC 60112 | PLC 3 | ||
| 100Hz | IEC 60250 | 0.016 | |
| 60Hz | IEC 60250 | 9E-03 | |
| 50Hz | IEC 60250 | 9E-03 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | UL 746 | PLC 0 | |
| 3.20mm, In oil | IEC 60243-1 | 18 KV/mm | |
| 0.800mm, In oil | IEC 60243-1 | 29 KV/mm | |
| 1.60mm, In oil | IEC 60243-1 | 25 KV/mm | |
| 3.20mm, inoil | ASTM D149 | 18 KV/mm | |
| 16mm, inoyl | ASTM D149 | 25 KV/mm | |
| 0.800mm, inoil | ASTM D149 | 29 KV/mm | |
| Volume resistivity | ASTMD257 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Horizontal: 23 to 150 ° C | ISO 11359-2 | 1.5E-04 cm/cm/°C | |
| Horizontal: 23 to 80 ° C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| Flow: 23 to 150 ° C | ISO 11359-2 | 3.9E-05 cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 9E-05 cm/cm/°C | |
| ISO 11359-2 | 7E-05 cm/cm/°C | ||
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 115 °C | |
| ball-indentation hardness | IEC 60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 4E-05 cm/cm/°C | |
| ISO 11359-2 | 3.7E-05 cm/cm/°C | ||
| Flow: 23 to 80 ° C | ISO 11359-2 | 4E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 175 °C | |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 135 °C | |
| 1.8MPa, Unanealed, 3.20mm | ASTM D648 | 115 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.