PBT VX5011 SABIC INNOVATIVE US
VALOX™ 
chip、Electronic and Electrical
Low warpage、Aging resistance、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
-30°CISO 179/2C6.0 kJ/m²
23°CISO 180/1A6.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376337.0 J
23°CISO 179/1eU40 kJ/m²
-30°CASTM D25647 J/m
ISO 179/1eA4.0 kJ/m²
ASTM D4812470 J/m
ISO 179/1eU30 kJ/m²
ISO 179/2U40 kJ/m²
23°CISO 179/1eA4.0 kJ/m²
0°CASTM D25647 J/m
23°CISO 180/1U40 kJ/m²
ASTM D25647 J/m
-30°CISO 180/1A5.0 kJ/m²
23°CISO 179/2C6.0 kJ/m²
ASTM D4812480 J/m
0°CISO 180/1A5.0 kJ/m²
-30°CISO 180/1U30 kJ/m²
Supplementary InformationTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
fillerASTM D22910 %
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
ball-indentation hardnessH358/30ISO 2039-1165 Mpa
Rockwell hardnessR计秤ISO 2039-2122
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
1.60mm, In oilIEC 60243-125 KV/mm
Volume resistivityASTMD257>1.0E+15 ohms·cm
High arc combustion index (HAI)HAIUL 746PLC 0
3.20mm, In oilIEC 60243-118 KV/mm
60Hz60HzIEC 602509E-03
50Hz50HzIEC 602509E-03
Compared to the Leakage Tracking Index (CTI)解决方案BIEC 60112PLC 4
--IEC 60112PLC 3
0.800mm, In oilIEC 60243-129 KV/mm
0.800mm, inoilASTM D14929 KV/mm
100Hz100HzIEC 602500.016
Hot wire ignition (HWI)HWIUL 746PLC 0
16mm, inoylASTM D14925 KV/mm
Surface ResistivityIEC 60093>1.0E+15 ohms
3.20mm, inoilASTM D14918 KV/mm
1MHz1MHzASTMD1500.014
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
yieldASTM D6383.0 %
fractureISO 527-2/595.0 Mpa
yieldASTM D63890.0 Mpa
Yield, 50.0mm spanASTM D790126 Mpa
--3ASTM D6384600 Mpa
yieldISO 527-2/595.0 Mpa
ISO 527-2/53.0 %
fractureASTM D63890.0 Mpa
--11ISO 178130 Mpa
--10ISO 178140 Mpa
fractureASTM D6383.0 %
--9ISO 1784000 Mpa
Taber abraser1000Cycles,1000g,CS-17转轮内部方法54.0 mg
Fracture bending strainISO 1785.0 %
50.0mm spanASTM D7903600 Mpa
fractureISO 527-2/53.0 %
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
Burning wire flammability index3.00mmIEC 60695-2-12850 °C
UL flame retardant rating1.60mmUL 94HB
Burning wire flammability index1.00mmIEC 60695-2-12750 °C
Limiting Oxygen IndexISO 4589-221 %
Filling analysisTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
melt viscosity260°C,1500sec^-1ISO 11443145 Pa·s
physical property Test ConditionTest MethodSABIC INNOVATIVE US/VX5011
melt mass-flow rate265°C/5.0kgASTM D123885 g/10min
Shrinkage rateTD2内部方法0.50-0.90 %
MD:3.20mm内部方法0.40-0.60 %
densityASTMD7921.31 g/cm³
Melt volume flow rate250°C/5.0kgISO 113350.0 cm3/10min
melt mass-flow rate266°C/5.0kgASTM D123885 g/10min
Water absorption rate平衡,23°C,50%RHISO 620.10 %
饱和,23°CISO 620.15 %
Melt volume flow rate265°C/5.0kgISO 113375.0 cm3/10min
Shrinkage rateMD1内部方法0.30-0.80 %
Melt volume flow rate250°C/2.16kgISO 113318.0 cm3/10min
melt mass-flow rate200°C/3.8kgASTM D123818 g/10min
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/VX5011
Horizontal: 23 to 80 ° C横向, 23到80℃ISO 11359-29E-05 cm/cm/°C
Flow: -40 to 40 ° CASTME8314E-05 cm/cm/°C
ISO 11359-23.7E-05 cm/cm/°C
Flow: 23 to 150 ° C23到150℃ISO 11359-23.9E-05 cm/cm/°C
0.45MPa, Unanealed, 3.20mmASTM D648175 °C
Horizontal: 23 to 150 ° C横向, 23到150℃ISO 11359-21.5E-04 cm/cm/°C
Flow: 23 to 80 ° C23到80℃ISO 11359-24E-05 cm/cm/°C
Horizontal: -40 to 40 ° C横向, -40到40℃ISO 11359-27E-05 cm/cm/°C
横向, -40到40℃ASTME8319E-05 cm/cm/°C
0.45MPa, Unanealed, 64.0mm spanISO 75-2/Bf135 °C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af115 °C
1.8MPa, Unanealed, 3.20mmASTM D648115 °C
ball-indentation hardness125°CIEC 60695-10-2Pass