PA6 Durethan® BKV30 000000 ENVALIOR WUXI
631
- Unit Price:US$ 2,978 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:30MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30%｜Filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ball Pressure Test | ISO 2039-1 | 210 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 215 °C |
| 1.8MPa,Unannealed,4.00mm | ASTM D648 | 200 °C | |
| 1.8MPa,Unannealed | ISO 75-2/A | 200 °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 200 °C |
| -- | ISO 306/B120 | >200 °C | |
| Melting temperature | ISO 11357-3 | 222 °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO 11359-2 | 2E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
| RTI Elec | 1.5mm | UL 746 | 130 °C |
| RTI Imp | 0.8mm | UL 746 | 95.0 °C |
| Hot deformation temperature | 0.45MPa,Unannealed,4.00mm | ASTM D648 | 215 °C |
| RTI Imp | 1.5mm | UL 746 | 95.0 °C |
| RTI Str | 0.8mm | UL 746 | 130 °C |
| 1.5mm | UL 746 | 130 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 1.6mm | UL 94 | HB | |
| 3.0mm | UL 94 | HB | |
| 3.2mm | UL 94 | HB | |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 600 °C |
| Extreme Oxygen Index | ISO 4589-2 | 22 % | |
| BurningBehavior | >1.00mm | ISO 3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6.GR.14-100.GF30 |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Thin film puncture strength | --7 | ISO 6603-2 | 8.00 J |
| --8 | ISO 6603-2 | 6.00 J | |
| --8 | ISO 6603-2 | 950 N | |
| --7 | ISO 6603-2 | 1070 N |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Relative permittivity | 23°C,1MHz | IEC 60250 | 4.00 |
| Dissipation factor | 23°C,50Hz | IEC 60250 | 5E-03 |
| 23°C,100Hz | IEC 60250 | 5E-03 | |
| 23°C,1MHz | IEC 60250 | 0.0150.015 | |
| Arc resistance | ASTM D495 | -- sec | |
| Compared to the anti leakage trace index | ASTM D3638 | V | |
| SolutionA | IEC 60112 | V | |
| SolutionB | IEC 60112 | V | |
| Surface resistivity | IEC 60093 | 1E+14 ohms | |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC 60243-1 | 40 KV/mm |
| 23°C,3.00mm | IEC 60243-1 | 40 KV/mm | |
| Dielectric constant | 23°C,50Hz | IEC 60250 | 4.00 |
| 23°C,1MHz | IEC 60250 | 4.00 | |
| Relative permittivity | 23°C,100Hz | IEC 60250 | 4.00 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Melt Volume Flow Rate (MVR) | 260°C/5.0kg | ISO 1133 | 14.0 cm3/10min |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO 2577 | 0.82 % |
| TD:120°C,2hr,3.00mm3 | ISO 294-4 | 0.12 % | |
| MD:280°C,3.00mm2 | ISO 2577 | 0.16 % | |
| MD:120°C,2hr,3.00mm3 | ISO 2577 | 0.030 % | |
| Water absorption rate | Saturation,23°C | ISO 62 | 7.0 % |
| Equilibrium,23°C,50%RH | ISO 62 | 2.1 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ASTM D638 | 9200 Mpa |
| -5°C | ISO 527-2/1 | 9800 Mpa | |
| tensile strength | Break,23°C | ASTM D638 | 180 Mpa |
| Break,23°C | ISO 527-2/5 | 180 Mpa | |
| elongation | Break,23°C | ASTM D638 | 3.0 % |
| Tensile strain | Break,23°C | ISO 527-2/5 | 3.0 % |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| 1000hr | ISO 899-1 | -- Mpa | |
| Bending modulus | 23°C | ASTM D790 | 8270 Mpa |
| 23°C | ISO 178/A | 8600 Mpa | |
| bending strength | 23°C | ASTM D790 | 280 Mpa |
| 3.5%Strain | ISO 178/A | -- Mpa | |
| 23°C | ISO 178 | 280 Mpa | |
| FlexuralStrainatFlexuralStrength6(23°C) | 4.0 % |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 70 kJ/m² |
| 23°C | ISO 179/1eU | 80 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 60 kJ/m² |
| 23°C | ISO 180/1U | 75 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.