Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV30 000000 ENVALIOR WUXI
Durethan®
--
Glass fiber reinforced、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Notched Izod impact strength | -30°C | ISO180/1U | 60 kJ/m² |
| 23°C | ISO180/1U | 75 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 80 kJ/m² |
| -30°C | ISO179/1eU | 70 kJ/m² |
| hardness | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 210 Mpa |
| Supplementary Information | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6,GR,14-100,GF30 |
| film | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Film Puncture Force | --7 | ISO6603-2 | 1070 N |
| Film Puncture Energy | --7 | ISO6603-2 | 8.00 J |
| --8 | ISO6603-2 | 6.00 J | |
| Film Puncture Force | --8 | ISO6603-2 | 950 N |
| Electrical performance | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+14 ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC60243-1 | 40 KV/mm |
| arc resistance | ASTMD495 | -- sec | |
| Dissipation Factor | 23°C,50Hz | IEC60250 | 5E-03 |
| 23°C,1MHz | IEC60250 | 0.0150.015 | |
| CTI | ASTMD3638 | -- V | |
| Relative Permittivity | 23°C,100Hz | IEC60250 | 4.00 |
| 23°C,1MHz | IEC60250 | 4.00 | |
| dielectric constant | 23°C,1MHz | IEC60250 | 4.00 |
| 23°C,50Hz | IEC60250 | 4.00 | |
| CTI | 解决方案A | IEC60112 | 600 V |
| 解决方案B | IEC60112 | 400 V | |
| Dissipation Factor | 23°C,100Hz | IEC60250 | 5E-03 |
| dielectric strength | 23°C,3.00mm | IEC60243-1 | 40 KV/mm |
| Mechanical properties | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Tensile modulus | -5°C | ISO527-2/1 | 9800 Mpa |
| TensileCreepModule | 1hr | ISO899-1 | -- Mpa |
| elongation | 断裂,23°C | ASTMD638 | 3.0 % |
| Tensile stress | 断裂,23°C | ISO527-2/5 | 180 Mpa |
| tensile strength | 断裂,23°C | ASTMD638 | 180 Mpa |
| Bending stress 5 | 23°C | ISO178 | 280 Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | -- Mpa |
| Bending stress 5 | 3.5%Strain | ISO178/A | -- Mpa |
| Tensile modulus 4 | 23°C | ASTMD638 | 9200 Mpa |
| Flexural modulus | 23°C | ISO178/A | 8600 Mpa |
| 23°C | ASTMD790 | 8270 Mpa | |
| Tensile strain | 断裂,23°C | ISO527-2/5 | 3.0 % |
| bending strength | 23°C | ASTMD790 | 280 Mpa |
| Bending stress 5 | FlexuralStrainatFlexuralStrength6(23°C) | 4.0 % |
| flammability | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 600 °C |
| Extreme Oxygen Index 11 | ISO4589-2 | 22 % | |
| UL flame retardant rating | 3.0mm | UL94 | HB |
| 3.2mm | UL94 | HB | |
| 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | |
| 1.6mm | UL94 | HB | |
| BurningBehavior12 | >1.00mm | ISO3795 | passed |
| physical property | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.1 % |
| 饱和,23°C | ISO62 | 7.0 % | |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO2577 | 0.030 % |
| TD:280°C,3.00mm2 | ISO2577 | 0.82 % | |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 14.0 cm3/10min |
| Apparent density | ISO60 | 0.70 g/cm³ | |
| Shrinkage rate | MD:280°C,3.00mm2 | ISO2577 | 0.16 % |
| TD:120°C,2hr,3.00mm3 | ISO294-4 | 0.12 % |
| Thermal performance | Test Condition | Test Method | ENVALIOR WUXI/BKV30 000000 |
|---|---|---|---|
| RTI Str | 0.8mm | UL746 | 130 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 200 °C |
| Linear thermal expansion coefficient | MD：23到55°C | ISO11359-2 | 2E-05 cm/cm/°C |
| vicat | -- | ISO306/B50 | 200 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 215 °C |
| 1.8MPa,未退火,4.00mm | ASTMD648 | 200 °C | |
| Linear thermal expansion coefficient | TD：23to55°C | ISO11359-2 | 8E-05 cm/cm/°C |
| RTI Elec | 1.5mm | UL746 | 130 °C |
| RTI Str | 1.5mm | UL746 | 130 °C |
| RTI Imp | 1.5mm | UL746 | 95.0 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,4.00mm | ASTMD648 | 215 °C |
| RTI Imp | 0.8mm | UL746 | 95.0 °C |
| vicat | -- | ISO306/B120 | >200 °C |
| Melting temperature 5 | ISO11357-3 | 222 °C |