MBS 165 INEOS STYRO USA
292
- Unit Price:US$ 2,838 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:28MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Vicat softening temperature | ASTM D15252 | 93.9 °C | |
| Maximum operating temperature | 250 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Refractive index | ASTM D542 | 1.570 | |
| ISO 489 | 1.570 | ||
| transmissivity | 550nm | ASTM D1003 | 90.0 % |
| turbidity | ASTM D1003 | 2.2 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.04 g/cm³ | |
| ISO 1183 | 1.04 g/cm³ | ||
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 5.0 g/10min |
| Melt Volume Flow Rate (MVR) | 200°C/5.0kg | ISO 1133 | 5.00 cm3/10min |
| Shrinkage rate | MD | ASTM D955 | 0.20-0.60 % |
| ISO 294-4 | 0.20-0.60 % | ||
| Water absorption rate | Saturation,23°C | ASTM D570 | 0.10 % |
| Saturation,23°C | ISO 62 | 0.10 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | Yield,23°C | ASTM D638 | 20.7 Mpa |
| Yield,23°C | ISO 527-2 | 21.0 Mpa | |
| elongation | Break | ASTM D638 | 50 % |
| Bending modulus | ASTM D790 | 1550 Mpa | |
| ISO 178 | 1650 Mpa | ||
| bending strength | ASTM D790 | 37.2 Mpa | |
| ISO 178 | 37.0 Mpa | ||
| Rockwell hardness | M-Scale | ASTM D785 | 70 |
| Tensile modulus | ASTM D638 | 1520 Mpa | |
| ISO 527-2 | 1520 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.