PC LEXAN™ XHT3141 BK1C141 SABIC INNOVATIVE US

264

Unit Price:US$ 5,490 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance
Application Areas:Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	68.0	J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875	°C
Metallic haze	起始	Internal Method	165	°C
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	50.0 mm Span4	ASTM D790	2600	Mpa
elongation	Break	ISO 527-2/50	70	%
	elongation	Break3	ASTM D638	70	%
		elongation	Yield	ISO 527-2/50	6.0	%
		elongation	elongation	Yield3	ASTM D638	6.0	%
tensile strength	Break	ISO 527-2/50	60.0	Mpa
	tensile strength	Break3	ASTM D638	55.0	Mpa
		tensile strength	Yield	ISO 527-2/50	70.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	70.0	Mpa
Tensile modulus	--	ISO 527-2/1	2500	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2700	Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	120	Mpa
bending strength	bending strength	--5,6	ISO 178	80.0	Mpa
Bending modulus	--5	ISO 178	2500	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			135	°C
Suggested injection volume			40 to 60	%
drying time			4.0 to 6.0	hr
Suggested maximum moisture content			0.020	%
Temperature at the rear of the barrel			270 to 330	°C
Temperature in the middle of the barrel			280 to 340	°C
Temperature at the front of the material cylinder			290 to 350	°C
Spray nozzle temperature			285 to 345	°C
Processing (melt) temperature			290 to 350	°C
Mold temperature			95 to 130	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 90	rpm
Exhaust hole depth			0.025 to 0.080	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	166	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Bf	164	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	156	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	152	°C
Vicat softening temperature	--	ASTM D152510	170	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	168	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.0E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.0E-5	cm/cm/°C
thermal conductivity	25°C	ASTM C177	0.20	W/m/K
RTI Elec		UL 746	150	°C
RTI Imp		UL 746	130	°C
RTI		UL 746	150	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.30	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.90	%
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	30.0	cm3/10min
melt mass-flow rate	330°C/2.16 kg	ASTM D1238	33	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		UL 746	PLC 3
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3
Surface resistivity		ASTM D257	> 1.0E+17	ohms
Volume resistivity		ASTM D257	> 1.0E+17	ohms·cm
Dielectric strength	3.20 mm, in Oil	ASTM D149	23	KV/mm
Dielectric constant	100 Hz	ASTM D150	2.90
Dielectric constant	Dielectric constant	1 MHz	ASTM D150	2.80
Dissipation factor	100 Hz	ASTM D150	0.031
Dissipation factor	Dissipation factor	1 MHz	ASTM D150	0.011

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Shenzhen Jiuhe	US$ 9330 /MT

Supplier Join

Get App

Top

PC LEXAN™ XHT3141 BK1C141 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index