PC XHT3141 BK1C141 PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC SABIC INNOVATIVE US XHT3141 BK1C141

Injection grade

US$ 5,490 / MT

FOB Guangzhou port, China

injection	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
Back pressure			0.300 to 0.700 Mpa
Temperature at the front of the material cylinder			290 to 350 °C
Screw speed			40 to 90 rpm
Mold temperature			95 to 130 °C
Processing (melt) temperature			290 to 350 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
Spray nozzle temperature			285 to 345 °C
Exhaust hole depth			0.025 to 0.080 mm
drying temperature			135 °C
Temperature in the middle of the barrel			280 to 340 °C
drying time			4.0 to 6.0 hr
Temperature at the rear of the barrel			270 to 330 °C
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
bending strength	--5,6	ISO 178	80.0 Mpa
Bending modulus	50.0 mm Span4	ASTM D790	2600 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	120 Mpa
elongation	Break	ISO 527-2/50	70 %
		Yield3	ASTM D638	6.0 %
		Yield	ISO 527-2/50	6.0 %
		Break3	ASTM D638	70 %
tensile strength	Break	ISO 527-2/50	60.0 Mpa
		Yield	ISO 527-2/50	70.0 Mpa
		Yield3	ASTM D638	70.0 Mpa
Tensile modulus	--2	ASTM D638	2700 Mpa
Tensile modulus		--	ISO 527-2/1	2500 Mpa
Bending modulus	--5	ISO 178	2500 Mpa
tensile strength	Break3	ASTM D638	55.0 Mpa
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Bf	164 °C
Linear coefficient of thermal expansion	Across Flow : -40°C	ISO 11359-2	6.0E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9	ISO 75-2/Af	152 °C
Hot deformation temperature		0.45 MPa, Unannealed, 3.20 mm	ASTM D648	166 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.0E-5 cm/cm/°C
thermal conductivity	25°C	ASTM C177	0.20 W/m/K
Vicat softening temperature	--	ISO 306/B50	168 °C
RTI Elec		UL 746	150 °C
RTI Imp		UL 746	130 °C
RTI		UL 746	150 °C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	156 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ASTM D152510	170 °C
flammability	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	875 °C
Metallic haze	起始	Internal Method	165 °C
UL flame retardant rating	3.0 mm	UL 94	HB
Burning wire flammability index	3.0 mm	IEC 60695-2-12	960 °C
UL flame retardant rating	1.5 mm	UL 94	HB
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
Surface resistivity		ASTM D257	> 1.0E+17 ohms
Compared to the anti leakage trace index		UL 746	PLC 3
Dissipation factor	1 MHz	ASTM D150	0.011
Dielectric constant	1 MHz	ASTM D150	2.80
Dissipation factor	100 Hz	ASTM D150	0.031
Dielectric strength	3.20 mm, in Oil	ASTM D149	23 KV/mm
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 3
Dielectric constant	100 Hz	ASTM D150	2.90
Volume resistivity		ASTM D257	> 1.0E+17 ohms·cm
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
Water absorption rate	Saturation, 23°C	ISO 62	0.30 %
Melt Volume Flow Rate (MVR)	330°C/2.16 kg	ISO 1133	30.0 cm3/10min
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.30 %
melt mass-flow rate	330°C/2.16 kg	ASTM D1238	33 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.60 - 0.90 %
impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/XHT3141 BK1C141
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	68.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	11 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂