ABS

ABS STAREX® HG-0760AT Samsung Cheil South Korea

285

Unit Price:US$ 2,803 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜Antistatic｜High impact resistance
Application Areas:Electrical enclosure｜Automotive Applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	18 kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	220 J/m
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	210 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	16 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	61.0 Mpa
bending strength	bending strength		ISO 178	63.0 Mpa
Tensile modulus		ASTM D638	2100 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/50	2400 Mpa
tensile strength	Yield	ASTM D638	39.0 Mpa
	tensile strength	Yield	ISO 527-2/50	42.0 Mpa
		tensile strength	Break	ASTM D638	33.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	34.0 Mpa
elongation	Break	ASTM D638	37 %
Tensile strain	Break	ISO 527-2/50	20 %
Bending modulus		ASTM D790	2200 Mpa
Bending modulus	Bending modulus		ISO 178	2200 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306/B50	94.0 °C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	82.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	82.0 °C

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.04 g/cm³
density	density		ISO 1183	1.04 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTM D1238	3.5 g/10min
melt mass-flow rate	melt mass-flow rate	200°C/5.0kg	ISO 1133	3.5 g/10min
Shrinkage rate	MD：3.20mm	ASTM D955	0.34-0.42 %
	Shrinkage rate	TD：3.20mm	ASTM D955	0.36-0.45 %
		Shrinkage rate	TD:3.20mm	ISO 2577	0.36-0.45 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ISO 2577	0.34-0.42 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	109
Rockwell hardness	Rockwell hardness	R-Scale	ISO 2039-2	109

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS STAREX® HG-0760AT Samsung Cheil South Korea

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet