Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS HG-0760AT Samsung Cheil South Korea
STAREX®
Electrical enclosure、Automotive Applications
High mobility、Antistatic、High impact resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Samsung Cheil South Korea/HG-0760AT |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 18 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 210 J/m |
| 23°C | ISO 180/1A | 16 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 220 J/m |
| hardness | Test Condition | Test Method | Samsung Cheil South Korea/HG-0760AT |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 109 |
| R级 | ASTM D785 | 109 |
| Mechanical properties | Test Condition | Test Method | Samsung Cheil South Korea/HG-0760AT |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 42.0 Mpa |
| elongation | 断裂 | ASTM D638 | 37 % |
| Tensile modulus | ISO 527-2/50 | 2400 Mpa | |
| bending strength | ISO 178 | 63.0 Mpa | |
| ASTM D790 | 61.0 Mpa | ||
| Flexural modulus | ISO 178 | 2200 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 33.0 Mpa |
| 屈服 | ASTM D638 | 39.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 20 % |
| Flexural modulus | ASTM D790 | 2200 Mpa | |
| tensile strength | 断裂 | ISO 527-2/50 | 34.0 Mpa |
| physical property | Test Condition | Test Method | Samsung Cheil South Korea/HG-0760AT |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 3.5 g/10min |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.34-0.42 % |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 3.5 g/10min |
| Shrinkage rate | TD:3.20mm | ISO 2577 | 0.36-0.45 % |
| TD：3.20mm | ASTM D955 | 0.36-0.45 % | |
| density | ASTM D792 | 1.04 g/cm³ | |
| ISO 1183 | 1.04 g/cm³ | ||
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.34-0.42 % |
| Thermal performance | Test Condition | Test Method | Samsung Cheil South Korea/HG-0760AT |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 82.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 82.0 °C | |
| vicat | ISO 306/B50 | 94.0 °C |