Material Properties:Non chloro non bromine flame retardant｜heat conduction
Application Areas:Lighting applications｜Electronic and Electrical Applications｜Plastic bag
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 3.20 mm	ASTM D648	227 °C
	Heat Deflection Temperature	0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8	ISO 75-2/Bf	228 °C
		Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm	ASTM D648	215 °C
		Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8	ISO 75-2/Af	208 °C
ball-indentation hardness	123 到 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	流动 : 40 到 120°C	ASTM E831	4.1E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向 : 40 到 120°C	ASTM E831	8.5E-5 cm/cm/°C
thermal conductivity	--9	ASTM E1461	1.4 W/m/K
	thermal conductivity	--10	ASTM E1461	1.8 W/m/K
		thermal conductivity	--11	ISO 22007-2	0.90 W/m/K
		thermal conductivity	thermal conductivity	--12	ISO 22007-2	1.9 W/m/K
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	105 °C
RTI		UL 746	120 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	V-0
Burning wire flammability index	1.0 到 3.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	750 °C
Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	800 °C

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	流动 : 24小时	ASTM D955	0.42 %
shrinkage rate	shrinkage rate	横向流动 : 24小时	ASTM D955	0.58 %
water absorption rate	24 hr, 23°C	ISO 62	0.040 %
	water absorption rate	24 hr, 23°C2	ISO 62	0.23 %
	water absorption rate	water absorption rate	平衡, 23°C, 50% RH	ISO 62	0.040 %

Electrical performance	Test Condition	Test Method	Test Result
surface resistivity		ASTM D257	> 1.0E+15 ohms
dielectric strength	1.00 mm, in Oil	ASTM D149	> 10 KV/mm
dielectric constant	1.10 GHz	ASTM ES7-83	4.84
Dissipation Factor	1.10 GHz	ASTM ES7-83	9.9E-3
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V
High arc combustion index (HAI)		UL 746	PLC 0
Hot wire ignition (HWI)		UL 746	PLC 3

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 hr
Suggested maximum moisture content			0.15 to 0.25 %
Temperature at the rear of the barrel			260 to 275 °C
Temperature in the middle of the barrel			270 to 290 °C
Temperature at the front of the material cylinder			270 to 290 °C
Processing (melt) temperature			270 to 295 °C
mold temperature			85 to 100 °C
Back pressure			0.200 to 0.300 Mpa
screw speed			20 to 60 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile modulus	--3	ASTM D638	13300 Mpa
tensile modulus	tensile modulus	--	ISO 527-2/1	13300 Mpa
tensile strength	断裂4	ASTM D638	98.0 Mpa
tensile strength	tensile strength	断裂	ISO 527-2/5	108 Mpa
elongation	断裂4	ASTM D638	1.3 %
elongation	elongation	断裂	ISO 527-2/5	1.3 %
flexural modulus	50.0 mm 跨距5	ASTM D790	12500 Mpa
flexural modulus	flexural modulus	--6	ISO 178	13000 Mpa
bending strength	--6,7	ISO 178	186 Mpa
	bending strength	屈服, 50.0 mm 跨距5	ASTM D790	167 Mpa
	bending strength	bending strength	断裂, 50.0 mm 跨距5	ASTM D790	176 Mpa

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	330 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C8	ISO 180/1U	23 kJ/m²

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.